Abstract:The capture of carbon dioxide (CO 2 ) has attracted significant attention to reduce the emissions of greenhouse gases. However, the development of adsorptive materials remains to be a grand challenge. In this work, we successfully synthesized low silica X (LSX) zeolites from low-grade coal gangue (mass ratio of Al 2 O 3 /SiO 2 < 0.50), a major byproduct in the coal mining industry, without additional Si or Al source via a two-step activation method (TA). The LSX zeolite had a Si/Al mole ratio of 1.05 and a specific surface area of 634 m 2 /g. Synthesis conditions including calcination temperature, alkali fusion temperature, potassium hydroxide dosage and crystallization time were systematically investigated to understand the reaction mechanism and optimize the synthesis conditions. Results showed that quartz was the main impurity remained in the product and thermal activation at 1200 °C was beneficial to decompose quartz and suppress the formation of sodalite impurity. Zeolite A could be eliminated by optimizing potassium hydroxide dosage and crystallization time. Compared to the conventional alkali fusion method and calcination activation method, the zeolites synthesized via TA method had better crystallinity and higher purity. The LSX product showed a high CO 2 uptake of 4.99 mmol/g at 298 K and 1 bar. The ideal adsorption solution theory (IAST) selectivity of CO 2 /N 2 (15/85) and CO 2 /CH 4 (50/50) were 376 and 200 at 298 K and 1 bar, respectively. The separation performance was further demonstrated using Aspen Adsorption and results showed a high purity and recovery of 92.6% and 91.3%, respectively, while using 50% CO 2 in N 2 as the feed gas at the adsorption pressure of 211 kPa and desorption pressure of 22 kPa.

Zeolite-X synthesized from halloysite nanotubes and its application in CO2 capture

CO 2 capture using low silica X zeolite synthesized from low-grade coal gangue via a two-step activation method

Synthesis of pure zeolite X from coal slime

Synthesis, characterisation and CO2 adsorption potential of NaA and NaX zeolites and hydrotalcite obtained from the same coal fly ash

Synthesis of zeolite molecular sieve 13X from coal-fired slag for efficient room temperature CO2 adsorption

Synthesis of Pure Na–X and Na–P Zeolite from Acid-Extracting Residues of CFB Fly Ash by a Single-Step Hydrothermal Method

Selective Preparation of NaX Zeolite from Natrual Materials by Directing Agent Method

Preparation of Zeolite X by the Aluminum Residue From Coal Fly Ash for the Adsorption of Volatile Organic Compounds

Controllable Preparation of Cubic Zeolite A and Application of Langmuir Model in Carbon Dioxide Adsorption

Synthesis and characterization of zeolites NaA and NaX from coal gangue

Fast synthesis of highly crystallized LSX zeolite with boosted carbon dioxide hydrogenation activity

Synthesis of zeolites from low-cost feeds and its sustainable environmental applications

Capture CO2 from N2 and CH4 by zeolite L with different crystal morphology

Synthesis of NaHS zeolite using microwave assisted alkali activation of coal fly ash: preparation, mechanism, application

Microporous Carbon Coated Zeolite Particles for Efficient Carbon Capture from Wet Flue Gas

Methylcellulose-Directed Synthesis of Nanocrystalline Zeolite NaA with High CO2 Uptake

Zeolites Derived from Natural Kaolinite for CO2 Adsorption

Synthesis Of Ssz-13 Zeolite With High Molar Ratio Of Sio2 To Al2o3 By Crystal Transformation Method Using Tetraethyl Ammonium Hydroxide As Template

Synthesis of Zsm-5 Aggregates Made of Zeolite Nanocrystals Through A Simple Solvent-Free Method

Synthesis of Mesoporous Zeolite Single Crystals with Cheap Porogens

Sustainable and Efficient Synthesis of Nanosized EMT Zeolites under Solvent-Free and Organotemplate-Free Conditions