EFFECT OF MANGANESE DOPING ON MICROSTRUCTURE AND PROPERTIES OF PNW-PMS-PZT CERAMICS

DU Hongliang,DU Hongna,Zhou Wancheng,PEI Zhibin,Qu Shaobo

DOI: https://doi.org/10.3321/j.issn:0454-5648.2005.06.023

2005-01-01

Abstract:Piezoelectric ceramics Pb(Ni_(1/2)W_(1/2))O_3Pb(Mn_(1/3)Sb_(2/3))O_3Pb(Ti, Zr)O_3x MnO_2(PNWPMSPZTMnO_2) were prepared by the traditional ceramics process. The phase structure of ceramics sintered at 1 150 ℃ for 2 h was analyzed. The results show that the ceramics samples obtained are all in the pure perovskite phase, and no other phase is found. The grain size of the ceramic is increased with the increase of Mn doping amount. The effect of Mn doping on dielectric and piezoelectric properties was investigated in details. When the mass content x of MnO_2 is less than 0.2%, the dielectric constant e_r, piezoelectric constant d_(33) and mechanical quality factor Q_m increase, while dielectric loss tanδ decreases. When the content of MnO_2 is more than 0.2% e_r, d_(33) and Q_m are decreased, while tanδ is increased. With the increase of the amount of MnO_2, the mechanical coupling factor k_p and Curie temperature θ_C are decreased. The piezoelectric ceramics with 0.2% MnO_2 doping are most suitable for fabricating high-power piezoelectric transformer, the piezoelectric properties of which are e_r=2 138, tanδ=(0.005 8), k_p=0.613, Q_m=1 275, d_(33)=(380 pC/N), θ_C=205 ℃, respectively.