Enhanced Electromechanical Properties in MnCO3‐modified Pb(Ni,Nb)O3–PbZrO3–PbTiO3 Ceramics Via Defect and Domain Engineering

Shuhao Wang,Xiang Li,Jiajia Wang,Xiaojun Wu,Ling Li,Ji Zhang,Yaojin Wang

DOI: https://doi.org/10.1111/jace.18905

IF: 4.186

2022-01-01

Journal of the American Ceramic Society

Abstract:The development of piezoelectric ceramics with both large piezoelectric responses and mechanical quality factor is still a key challenge for practical applications for high-power piezoelectric devices. Here we report the strategy to utilize the synergistic contribution of engineered defect and domain structure, in which an excellent piezoelectric coefficient d(33) of 655 pC N-1 and mechanical quality factor Q(m) of 371 are simultaneously achieved in MnCO3-modified Pb(Ni,Nb)O-3-PbZrO3-PbTiO3 (Mn-PNN-PZ-PT) ceramics. Meanwhile, the depolarization temperature (T-d) and the temperature corresponding to the epsilon(r,max) (T-m) are enhanced relative to the pure counterpart. After annealing at 90 degrees C, the sample with x = 0.3 shows the retained d(33) value of 610 pC N-1, about 2.6 times larger than that with x = 0 counterpart, demonstrating a wider operating temperature range. These enhanced electromechanical properties originate from the internal bias field introduced by the defect dipoles (Mn-Zr,Mn-Ti ''-V-O(center dot center dot))(X) and (Mn-Nb '''-V-O(center dot center dot))'. It is verified that xMn-PNN-PZ-PT ceramics have superior potential for high-power application, meanwhile, paves a significant step toward enhancing the thermal stability of high-temperature piezoceramics.