Enhanced piezoelectricity in Pb(Zr0.48Ti0.52)O3-Pb(Mn1/3Sb2/3)O3-Pb(Mg1/3Ta2/3)O3 ceramics through the synergistic effect of defect engineering and lattice distortion
Yihan Ma,Mo Zhao,Dongyan Zhang,Zhimin Li,Maolin Zhang,Li Jin,Yangxi Yan
DOI: https://doi.org/10.1016/j.jallcom.2023.171779
IF: 6.2
2023-12-01
Journal of Alloys and Compounds
Abstract:With the increasing demand for industrial applications, it has become crucial to develop special high-power devices that can achieve both high piezoelectric performance and large mechanical quality factor. In this work, we prepared quaternary piezoelectric ceramics, namely (0.95-x)Pb(Zr0.48Ti0.52)O3-xPb(Mg1/3Ta2/3)O3-0.05Pb(Mn1/3Sb2/3)O3 (PZT-PMT-PMS), using a traditional solid-state route. These ceramics exhibit an excellent mechanical quality factor and low loss. By adding an appropriate amount of PMT (x = 0.09), the Mg2+ ions were homogeneously incorporated into the crystal lattice, resulting in a reduction in the content of the tetragonal phase. The formation of ( Mg Zr , Ti ′′ − V O . . ) defect dipoles has been studied through Rietveld refinement, which indicates that defect dipoles can hinder domain-wall motion, strengthen the pinning effect, and result in a “harder” performance. Moreover, the high asymmetry caused by large lattice distortion, regulates the piezoelectric properties. The sample shows the optimal performance when the PMT content is 0.09, with d 33 = 430 pC/N, Q m = 1740, T C = 258 °C, ε r = 1740, tanδ = 0.16 %, P r = 44.5μC/cm2, and k p = 0.569.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering