Decimeter-Scale Atomically Thin Graphene Membranes for Gas–Liquid Separation
Dandan Hou,Shengping Zhang,Xiaobo Chen,Ruiyang Song,Dongxu Zhang,Ayan Yao,Jiayue Sun,Wenxuan Wang,Luzhao Sun,Buhang Chen,Zhongfan Liu,Luda Wang
DOI: https://doi.org/10.1021/acsami.0c23013
2021-02-18
Abstract:Graphene holds great potential for fabricating ultrathin selective membranes possessing high permeability without compromising selectivity and has attracted intensive interest in developing high-performance separation membranes for desalination, natural gas purification, hemodialysis, distillation, and other gas–liquid separation. However, the scalable and cost-effective synthesis of nanoporous graphene membranes, especially designing a method to produce an appropriate porous polymer substrate, remains very challenging. Here, we report a facile route to fabricate decimeter-scale (∼15 × 10 cm<sup>2</sup>) nanoporous atomically thin membranes (NATMs) via the direct casting of the porous polymer substrate onto graphene, which was produced by chemical vapor deposition (CVD). After the vapor-induced phase-inversion process under proper experimental conditions (60 °C and 60% humidity), the flexible nanoporous polymer substrate was formed. The resultant skin-free polymer substrate, which had the proper pore size and a uniform spongelike structure, provided enough mechanical support without reducing the permeance of the NATMs. It was demonstrated that after creating nanopores by the O<sub>2</sub> plasma treatment, the NATMs were salt-resistant and simultaneously showed 3–5 times higher gas (CO<sub>2</sub>) permeance than the state-of-the-art commercial polymeric membranes. Therefore, our work provides guidance for the technological developments of graphene-based membranes and bridges the gap between the laboratory-scale "proof-of-concept" and the practical applications of NATMs in the industry.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c23013?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c23013</a>.Different adhesion performance of graphene to the substrates, schematic of the three-component phase diagram for a polymer/solvent/nonsolvent system, digital photographs of membranes at different times during the two types of phase-inversion processes, distribution of the pore size and open porosity data of the PVDF membranes, SEM images of the PVDF membranes prepared using the VIPS method under different temperature and humidity conditions, homogeneity characterization of the decimeter-scale polymeric membranes, SEM images of the decimeter-scale NATMs, SEM images of graphene on copper foil, diffusion-driven transport data of KCl through various membranes, and the digital photograph of the nanoporous graphene/polymer composite membrane after the CO<sub>2</sub> transport experiment (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c23013/suppl_file/am0c23013_si_001.pdf">PDF</a>).This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology