Abstract:Plant fiber-reinforced polylactic acid (PLA) exhibits excellent mechanical properties and environmental friendliness and, therefore, has a wide range of applications. This study investigated the mechanical properties of three short plant fiber-reinforced PLA composites (flax, jute, and ramie) using mechanical testing and material characterization techniques (SEM, FTIR, and DSC). Additionally, we propose a methodology for predicting the mechanical properties of high-content short plant fiber-reinforced composite materials. Results indicate that flax fibers provide the optimal reinforcement effect due to differences in fiber composition and microstructure. Surface pretreatment of the fibers using alkali and silane coupling agents increases the fiber–matrix interface contact area, improves interface performance, and effectively enhances the mechanical properties of the composite. The mechanical properties of the composites increase with increasing fiber content, reaching the highest value at 40%, which is 38.79% higher than pure PLA. However, further increases in content lead to fiber agglomeration and decreased composite properties. When the content is relatively low (10%), the mechanical properties are degraded because of internal defects in the material, which is 40.42% lower than pure PLA. Through Micro-CT technology, the fiber was reconstructed, and it was found that the fiber was distributed mainly along the direction of injection molding, and the twin-screw process changes the shape and length of the fiber. By introducing the fiber agglomeration factor function and correcting the Halpin-Tsai criterion, the mechanical properties of composite materials with different contents were successfully predicted. Considering the complex stress state of composite materials in actual service processes, a numerical simulation method was established based on transversely isotropic material using the finite element method combined with theoretical analysis. The mechanical properties of high-content short plant fiber-reinforced composite materials were successfully predicted, and the simulation results showed strong agreement with the experimental results.

Research Progress of Plant Fiber-Modified PLA

Current Research and Patents of Plant Fiber Composites

Modified Biomass-Reinforced Polylactic Acid Composites

A review of research and application of polylactic acid composites

Research Progress in the Synthesis and Modification of Polylactic Acid

PLA composites reinforced with rice residues or glass fiber—a review of mechanical properties, thermal properties, and biodegradation properties

PLA Composites Reinforced with Flax and Jute Fibers—A Review of Recent Trends, Processing Parameters and Mechanical Properties

3D‐printing continuous plant fiber/polylactic acid composites with lightweight and high strength

Technology Advances in Dyeing and Finishing Process of PLA Fibers and Fabrics

Mechanical Performances Analysis and Prediction of Short Plant Fiber-Reinforced PLA Composites

A Comprehensive Review on Mechanical Properties of Natural Cellulosic Fiber Reinforced PLA Composites

Mechanical properties of fibre/ filler based poly(Lactic Acid) (Pla) composites : A brief review

A comprehensive review on polylactic acid/lignin composites - Structure, synthesis, performance, compatibilization, and applications

Blending and functionalisation modification of 3D printed polylactic acid for fused deposition modeling

Study on properties of polylactic acid/lemongrass fiber biocomposites prepared by fused deposition modeling

Research progress in polylactic acid processing for 3D printing

Synergistic reinforcement of polylactic acid/wood fiber composites by cellulase and reactive extrusion

Natural Fiber-Reinforced Polylactic Acid, Polylactic Acid Blends and Their Composites for Advanced Applications

Mechanical and Thermal Properties of Bamboo Fiber–Reinforced PLA Polymer Composites: A Critical Study

Effects of fiber content on the properties of PLA/corn straw fiber composite foamed material

Preparation of Poly(lactic Acid) and Modified Starch Composites