Effects of Glass Fiber on Flame Retardant Performance, Mechanical Properties and Rheological Behavior of Flame-retardant POM Composites

Jun-liang WANG,Teng-fei QIN,Hao LI,Wen-kai ZHANG,Hao XU,Bao-ying LIU,Xiao-min FANG,Tao DING
DOI: https://doi.org/10.3969/j.issn.1005-5770.2017.10.021
2017-01-01
Abstract:Glass fiber (GF) reinforced intumescent flame retardants (IFR) flame-retardant modified polyoxymethylene (POM) composites was prepared by melt blending method.Mechanical and flame retardant properties of the flame-retardant polyoxymethylene system were investigated by vertical combustion test,limit oxygen index test,simple beam pendulum impact testing machine and universal mechanics tester.The rheological properties of the composites were measured by a rotary rheometer.The results show that compared with unreinforced system,the tensile strength and bending strength of POM/IFR composite system reinforced by 20wt% GF is increased by 15.8% and 16.0% respectively,and the impact strength is increased by 1 time.The POM/IFR/GF composites exhibits higher dynamic modulus and viscosity compared to the composites system without GF.Due to the "candle effect" from GF,POM/IFR/GF failed to achieve the UL-94 rating.After the surface modification of GF by phenolic resin,the limit oxygen index of POM/IFR/GF increases from 22.7% to 34.6%,the mechanical properties are improved slightly,the modulus and viscosity of the system are lower than that of the system with unmodified GF.
What problem does this paper attempt to address?