Effect of the Flame Retardants and Glass Fiber on the Polyamide 66/Polyphenylene Oxide Composites

Zhenya Zhang,Mingcheng Yang,Kunpeng Cai,Yang Chen,Shubo Liu,Wentao Liu,Jilin Liu

DOI: https://doi.org/10.3390/ma15030813

IF: 3.4

2022-01-21

Materials

Abstract:In this work, polyamide 66/polyphenylene oxide (PA66/PPO) composites, including the flame retardants 98 wt% aluminum diethylphosphinate + 2 wt% polydimethylsiloxane (P@Si), Al(OH)3-coated red phosphorus (RP*), and glass fiber (GF), were systematically studied, respectively. The limiting oxygen index (LOI), UL-94 vertical burning level, and thermal and mechanical properties of the PA66/PPO composites were characterized. The results showed that the P@Si and RP flame retardants both improved the LOI value and UL-94 vertical burning level of the PA66/PPO composites, and PA66/PPO composites passed to the UL-94 V-0 level when the contents of P@Si and RP* flame retardants were 16 wt% and 8 wt%. On the other hand, the mechanical properties of the PA66/PPO composites were reduced from a ductile to a brittle fracture mode. The addition of GF effectively made up for these defects and improved the mechanical properties of the PA66/PPO composites containing the P@Si and RP*, but it did not change the fracture mode. P@Si and RP* flame retardants improved the thermal decomposition of PA66/PPO/GF composites and reduced the maximum mass loss rates, showing that the PA66/PPO/GF composites containing the P@Si and RP* flame retardants could be used in higher-temperature fields.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering