Preparation of Phosphorus-Containing Poly-Acrylate Resins and their Flame Resistant Properties

Xiao-shuang WANG,Gui-long XU,Yi WANG,Yun LIANG,Jian HU

DOI: https://doi.org/10.3969/j.issn.1003-9015.2017.01.026

2017-01-01

Abstract:Phosphorous(P)-containing phosphoric acid methacryloyloxyethyl ester (PMOE) was synthesized with β-hydroxyethyl methacrylate (HEMA) and phosphorus pentoxide (P2O5), which was used to prepare P-containing poly-acrylate emulsion. The effects of PMOE content on polymerization stability and resin flame retardancy were studied. The chemical composition of the prepared P-containing poly-acrylate (PA) emulsion was characterized by FTIR, while the thermal stability and flame retardancy of the prepared P-containing PA resin was measured by TGA, LOI and UL-94 test, and the micro-morphology of the char residue from the P-containing PA resin was observed by SEM. The results show that P-containing PA emulsion with high monomer conversion, low gelation and good storage stability can be obtained when the P-containing monomer content is lower than 30%(wt). Char yield and LOI increase when the content of P-containing monomer increases, which results in better flame retardancy. When the P-containing monomer content is 30 %(wt), LOI of the resin is 29.5%, and the char yield is 54 %(wt) at 700℃. The resin can pass the V-0 level of the UL-94 test. SEM results indicate that phosphorous shows a condensed-phase flame retardant effect.