Synthesis and characterization of a DOPO-substitued organophosphorus oligomer and its application in flame retardant epoxy resins

Xin Wang,Yuan Hu,Lei Song,Hongyu Yang,Weiyi Xing,Hongdian Lu

DOI: https://doi.org/10.1016/j.porgcoat.2010.12.013

IF: 6.6

2011-01-01

Progress in Organic Coatings

Abstract:Advanced flame retardant epoxy resins with different contents of poly(DOPO substituted phenyl dimethanol pentaerythritol diphosphonate) (PFR) were prepared. PFR was synthesized from the polycondensation of DOPO-disubstituted benzenedimethanol (TDCA-DOPO) with pentaerythritol diphosphonate dichloride (SPDPC). The flame retardancy and thermal stability of the EP/PFR hybrids were investigated by limiting oxygen index (LOI), UL-94 test and thermogravimetric analysis (TGA) in air. LOI values increased from 21.5 for pure EP to 36.0 for phosphorus-containing resins, and UL-94 V-0 materials were obtained with the 15wt% PFR. The TGA results indicated that incorporation of PFR significantly enhanced the char yield and the thermal stability of char layer at higher temperature. Differential scanning calorimetry revealed that the EP/PFR composites possessed higher glass transition temperatures than phosphorus-free EP, which was consistent with dynamic mechanical analysis results. The thermal degradation behaviors of the EP/PFR composites were investigated by real time Fourier transform infrared spectra (RTFTIR), thermogravimetric analysis/infrared spectrometry (TG–IR) and direct pyrolysis/mass (DP–MS) analysis. The results suggested that the addition of PFR can reduce the release of combustible gas, trap the H and OH radicals by releasing the PO radical and induce the formation of char layer, thus retard the polymer degradation and combustion process.