Abstract:Novel double DOPO-grafted phthalonitrile flame retardant (DOPO-DBAPh) has been successfully synthesized via solution reaction with amino-substituted phthalonitrile monomer, bisphenol A, paraformaldehyde and 9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) as initial materials. The molecular structure of DOPO-DBAPh was investigated by FT-IR and H-1-NMR spectrum. Then, the DOPO-DBAPh was added into epoxy (EP) to construct DOPO-DBAPh/EP fire-retarding composites by casting forming method. The effect of different proportions of DOPO-DBAPh/EP fire-retarding composites on the microstructure, thermal, mechanical, flame retardancy and combustion behavior was investigated. It was found that the DOPO-DBAPh/EP fire-retarding composites have a high glass transition temperature (T-g = 156 similar to 179 degrees C), and also have excellent thermal stability (T-5% = 331.4 similar to 365.4 degrees C) and high flexural strength (96.1-139.8 MPa). When DOPO-DBAPh content is 5 wt%, the vertical burning grade and limiting oxygen index (LOI) of DOPO-DBAPh/EP composites reached V-0 and 29.6%, respectively. Furthermore, the cone calorimeter testing results showed that the addition of DOPO-BAPh can obviously inhibit the decom-position rate of cured substance at high temperature and accelerated the formation of dense carbon layer. When DOPO-BAPh content was 20 wt%, the total heat release rate (THR) and peak heat release rate (PHRR) of the DOPO-DBAPh/EP fire-retarding composites were decreased by 38.55% and 35.81% compared with that of cured EP. In a word, this work presents a good way for synthesizing economical and highly efficient flame retardant for use in the preparation of EP-based fire-retarding composites with excellent comprehensive performance. Highlights center dot Novel phosphorus-nitrogen flame retardant (DOPO-DBAPh) is developed. center dot 5 wt% DOPO-DBAPh significantly improves the fire safety of EP resin. center dot The DOPO-DBAPh/EP composites exhibit good thermal and mechanical properties.

Effect of gas‐condensed phase synergistic system of 9,10‐dihydro‐9‐oxo‐10‐phosphaphenanthrene‐10‐oxide and polydopamine on flame retardancy of epoxy resin

Highly Effective P–P Synergy of a Novel DOPO-Based Flame Retardant for Epoxy Resin

Study of the Synergistic Effect of Polyhedral Oligomeric Octadiphenylsulfonylsilsesquioxane and 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide on Flame-Retarded Epoxy Resins

Synergistic Effect of Phenyl Phosphoric Acid Derivatives and DOPO on Multifunctional Epoxy Resin: Fire Safety, Mechanical Properties, Transparency and Hydrophobicity

Research on the Synergistic Flame Retardation of Epoxy Resin Through Surface-Modified Aluminum Diethylphosphinate in Conjunction with DOPO and CFA

Synergistic effect of chitosan derivative and DOPO for simultaneous improvement of flame retardancy and mechanical property of epoxy resin

Synthesis of phosphaphenanthrene derivatives as flame retardants and their properties in epoxy resin composites

Two high-efficient DOPO-based phosphonamidate flame retardants for transparent epoxy resin

Synthesis and characterization of a DOPO-substitued organophosphorus oligomer and its application in flame retardant epoxy resins

A novel 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide‐based reactive flame retardant for epoxy resin: Synthesis, properties, and comparison

DOPO-based Derivatives with Different Phosphorous Oxidation States As Highly Efficient Flame Retardants for Epoxy Resins

Preparation of DOPO‐derived magnesium phosphate whisker and its synergistic effect with ammonium polyphosphate on the flame retardancy and mechanical property of epoxy resin

Preparation of Phosphorus-Nitrogen Flame Retardant DOPO-DBAPh and Its Flame Retarded Epoxy-Based Composites

Properties of Epoxy Resin Composites Containing 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide

Synthesis of a phosphorus–nitrogen-containing flame retardant and its application in epoxy resin

Synthesis of DOPO-PHBA reactive flame retardant and its effect on properties of epoxy resin with TGIC

Novel Flame Retardancy Effect of Phenethyl-Bridged DOPO Derivative on Epoxy Resin

Synergistic flame-retardant effect of expandable graphite and phosphorus-containing compounds for epoxy resin: Strong bonding of different carbon residues

Phenylenediamine‐phenyl Phosphonic Acid Salts Toward Good Flame Retardancy and Smoke Suppression Epoxy Resin

Synthesis, Structure-Property Relationships of DOPO-Phosphonamidates and Their Flame Retardant Application

Novel Flame Retardants Containing 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide and Unsaturated Bonds: Synthesis, Characterization, and Application in the Flame Retardancy of Epoxy Acrylates