Abstract:A series of hyperbranched polyphosphate acrylates (HPPAs) being used for UV curable flame retardant coatings were prepared by the reaction of tri(acryloyloxyethyl) phosphate (TAEP) with piperazine at given ratios, and characterized using FTIR, 1H NMR and GPC measurements. HPPA was blended with TAEP in different ratios to obtain a series of UV curable resins. Their maximum photopolymerization rates (RPmax) and final unsaturation conversion (Pf) in the cured films at the presence of a photofragmenting initiator were investigated. The results showed that the Pf increased along with HPPA content and the pure HPPA has the maximum value of 82.1% in the photo-DSC analysis. The data from dynamic mechanical thermal analysis showed that HPPA has good miscibility with TAEP. The crosslinking density and Tg of the cured film decrease along with the content of HPPA in the blend. The mechanical properties of the cured films were also investigated. Less than 20% HPPA addition improved both the tensile strength and elongation at break without damaging the modulus. The HPPA20TAEP80 film with 20% HPPA addition has the highest tensile strength of 31.7MPa and an elongation at break two times that of cured TAEP. The flame retardancy of the UV cured films was investigated by the limiting oxygen index (LOI). The cured TAEP/HPPA samples greatly expanded when burning, and the degree of expansion increased along with HPPA content. However, the LOI values decreased from 47.0 to 34.0 along with HPPA content, which can be ascribed to that the flame retardancy of TAEP is mainly acting in the gas phase, whereas HPPA mainly acting in condensed phase, and the gas phase mechanism holds the dominant effect while their blends are burning.

Synthesis and Properties of Novel Circular UV Curable Phosphorus-containing Acrylate

Synthesis of novel poly(aminophosphonate ester)s flame retardants and their applications in EVA copolymer

A New Intumescent Flame Retardant Containing Phosphorus and Nitrogen: Preparation, Thermal Properties and Application to UV Curable Coating

Synthesis of a Novel Phosphorus- and Nitrogen-Containing Acrylate and Its Performance As an Intumescent Flame Retardant for Epoxy Acrylate

Thermal and Uv-Curing Behavior of Phosphate Diacrylate Used for Flame Retardant Coatings

Preparation, Flame Retardancy and Thermal Behavior of a Novel UV-curable Coating Containing Phosphorus and Nitrogen

Combustion and Thermal Degradation Mechanism of a Novel Intumescent Flame Retardant for Epoxy Acrylate Containing Phosphorus and Nitrogen

A New Phosphorus Flame‐retard Curing Agent for Epoxy Resin/anhydride System

Synthesis and thermal behavior of a novel UV-curable transparent flame retardant film and phosphorus-nitrogen synergism of flame retardancy

Flame Retardancy and Thermal Properties of Novel UV-curing Epoxy Acrylate Coatings Modified by Phosphorus-Containing Hyperbranched Macromonomer

Preparation,flame retardancy and thermal properties of a novel phosphate modified UV-curable epoxy acrylate coating

Synthesis and properties of a novel phosphorous-containing flame-retardant hardener for epoxy resin

Preparation, Flame Retardancy, and Thermal Degradation of Unsaturated Polyester Resin Modified with A Novel Phosphorus Containing Acrylate

Preparation and Flame Retardant Properties of UV Curable Phosphorus-and Nitrogen-containing Acrylates

Synthesis and properties of a novel hyperbranched polyphosphate acrylate applied to UV curable flame retardant coatings

Photopolymerization behaviors of hyperbranched polyphosphonate acrylate and properties of the UV cured film

Flame Retardancy and Thermal Property of Novel Uv-Curable Epoxy Acrylate Coatings Modified by Melamine-Based Hyperbranched Polyphosphonate Acrylate

Synthesis and Properties of Phosphorus-contained Acrylate Emulsion

Synthesis, Characterization and Flame Retardancy of Methacrylated Phosphate/diphosphate

Synthesis and application in polypropylene of a novel of phosphorus-containing intumescent flame retardant.

Synthesis and properties of poly(bisphenol A acryloxyethyl phosphate) as a UV curable flame retardant oligomer