Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

Kinetic Study on Selective Catalytic Reduction of NOx by Br-Doped V2O5/TiO2 Catalysts

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Catalytic oxidation of CO over V2O5/TiO2 and V2O5-WO3/TiO2 catalysts: A DFT study

Selective Catalytic Removal of High Concentrations of NOx at Low Temperature

NOxRemoval over V2O5/WO3–TiO2Prepared by a Grinding Method: Influence of the Precursor on Vanadium Dispersion

Effects of Preparation Parameters on the DeNOx Performance of V2O5/TiO2 Catalysts

Effect of Dispersion State and Surface Properties of Supported Vanadia on the Activity of V2O5/TiO2 Catalysts for the Selective Catalytic Reduction of NO by NH3

Effects of CrOx species doping on V2O5-WO3/TiO2 catalysts on selective catalytic reduction of NOx by NH3 at low temperature

Bifunctional catalysts V-Cu/TiO 2 for selective catalytic reduction of NO x and CO oxidation under oxygen-rich conditions

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

Investigations of Surface VOx Species and Their Contributions to Activities of VOx/Ti0.5Sn0.5O2 Catalysts Toward Selective Catalytic Reduction of NO by NH3

Active sites of NO selective catalytic reduction over V2O5-WO3/TiO2

Ti3+ doped V2O5/TiO2 catalyst for efficient selective catalytic reduction of NOx with NH3

Mechanism of Selective Catalytic Reduction on VOx/TiO2 Catalyst by in Situ Ambient Pressure X-ray Photoelectron Spectroscopy

Highly Efficient Mesoporous V2O5/WO3–TiO2 Catalyst for Selective Catalytic Reduction of NOx: Effect of the Valence of V on the Catalytic Performance

Dynamic Change of Active Sites of Supported Vanadia Catalysts for Selective Catalytic Reduction of Nitrogen Oxides

In Situ DRIFTS Investigation on the SCR of NO with NH3 over V2O5 Catalyst Supported by Activated Semi-Coke

The Properties and SCR De‐nox Application of Supported V2O5/TiO2 Catalysts with Different Polymerization State of VOx Species Controlled by the Ph Value of Their Precursors

Performance of V_2O_5-WO_3-MoO_3/TiO_2 Catalyst for Selective Catalytic Reduction of NO_x by NH_3

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

Interface sites on vanadia-based catalysts are highly active for NOx removal under realistic conditions