Abstract:The control of the morphology of nanoparticles is a hot issue all over the world.Organic-inorganic materials can be tailor made with an infinite number of architectures and in diverse forms conveniently.A new type of organic inorganic hybrid material was reported to be synthesized by emulsion polymerization by using the monomers which contained alkoxysilane groups.However,polymerization and morphology could hardly be controled during the emulsion process, because the alkoxysilane group was easy to be subjected to hydrolysis and condensation by sol gel process which decreased the stability of the latex.In the present work, organic inorganic hybrid core shell nanoparticles were synthesized by seeded emulsion polymerization.Through morphology design, polystyrene, as seeded cores, was synthesized firstly, then 3 trimethoxysilyl propyl methacrylate (MPS) was added to form MPS styrene copolymer shell on the surface of polystyrene core. Owing to the hydrolysis condensation of organic alkoxysilane groups in MPS,the organic inorganic hybrid shell was formed through sol gel process.The core shell structure was interpreted by thermodynamical representation and characterized by transmission electron microscopy (TEM).The nonionic surfactant used would decrease the stability of the latex.In acidic condition the latex turned into gel just after the addition of MPS,while,in basic condition the particle number decreased obviously, and the latex kept almost stable in neutral condition.The higher the MPS concentration in the emulsion was,the less stability the latex had.Adding MPS continuously could keep the latex more stable and the particle size could be controlled by this method.Then, the core of this kind of hybrid nanoparticles could be dissolved to yield hollow nanocapsules, with the proportion of the void volume 40 1%.

The synthesis of cross-linked core-shell type microspheres and study of its structure and property

Optimising the Shell Thickness-To-Radius Ratio for the Fabrication of Oil-Encapsulated Polymeric Microspheres

An Improved Phase-Inversion Process for the Preparation of Silica/Poly[Styrene-Co-(Acrylic Acid)] Core-Shell Microspheres: Synthesis and Application in the Field of Polyolefin Catalysis

Synthesis of Monodisperse Silica Microspheres with Solid Core and Mesopore Shell

Preparation of Silica@Silica Core-Shell Microspheres Using an Aqueous Two-Phase System in a Novel Microchannel Device.

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

Synthesis of organic-inorganic hybrid core-shell nanoparticles and particle size control

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Synthesis of poly(methacrylic acid)-manganese oxide dihydroxide/silica core-shell and the corresponding hollow microspheres

Fabrication of hollow silica spheres and their application in polyacrylate film forming agent

Melt Rheology of Core-Shell Nanoparticles Filled Polystyrene

Preparation Of Monodisperse Silica/Pmma Core/Shell Nanoparticles With Controllable Shell Thickness By Soap-Free Emulsion Polymerization

Synthesis, investigation of temperature and salt resistant polyacrylamide microspheres used for deep sealing and profile control and function strengthening mechanism

Preparation and Characterization of Radially Porous Silica and the Core-shell Structure

Fabrication of Core-Shell Structured Mesoporous Silica Nanospheres with Dually Oriented Mesochannels Through Pore Engineering

Preparation and Performance Evaluation of Self-Cementing Nanoscale Polymeric Microspheres with Salt and Temperature Tolerance

Generalization of In-Situ Polymerization Method for Preparing Core-Shell Polymeric Nanospheres and Hollow Spheres

Research of the Synthesis and Film Performance of Silica/poly(st-Ba-mps) Core-Shell Latexes Obtained by Miniemulsion Co-Polymerization

Silicon dioxide hollow microspheres with porous composite structure: Synthesis and characterization

Silica-shell/oil-core microcapsules with controlled shell thickness and their breakage stress.

Synthesis of TiO2–SiO2/polymer Core–shell Microspheres with a Microphase‐inversion Method