Influence of Er Doping on the Microstructure and High-temperature Electrical Property of CaMnO3 Ceramics

Ya WEN,Cuiqin LI,Dongzhen ZHOU,Lijuan SUN,Jun LIU,Yu YAN

DOI: https://doi.org/10.16521/j.cnki.issn.1001-9642.2018.05.006

2018-01-01

Abstract:A series of Er-doped Ca1-xErxMnO3 (x=0, 0.02, 0.04, 0.06, 0.10) ceramics was synthesised by coprecipitation method and sintered at 1200 ℃ in air using mixed nitrate as the raw material. The phase structure and microscopic morphology of all the samples were characterized. And the electrical resistivity, Seebeck coefficient was simultaneously determined. The effects of Er doping on the microstructure and high-temperature electrical properties of CaMnO3 were investigated. The results of XRD and SEM show that the Ca1-xErxMnO3 ceramics synthesised by coprecipitation method has a single phase and the microstructure is dense. The results of electrical properties show that Er doping can effectively improve the electrical properties of CaMnO3 ceramics. The maximum power factor attained 2.95×10-4, with x=0.1 at 973 K, which is 1.5 times that of undoped CaMnO3.