Abstract:Abstract Because of the excellent fracture toughness and oxidation resistance, carbon short fiber reinforced ceramics have a sound potential for a variety of high‐temperature applications. For the composite's reliable use in long‐term applications, however, the oxidation effects on the mechanical strength are of crucial interest and have hitherto not been investigated in detail yet. In this study, the weight change of carbon short fiber reinforced C/SiC composites with carbon fiber lengths of 9 mm (long cut fiber composite – LCFC) and 2 mm (short milled fiber composite – SMFC), respectively, are evaluated in the temperature range from 500 to 1200 °C for two different fiber orientations. Both types of composites were additionally tested in bending mode after 25 and 50 min of exposure to air at 700 °C depending on fiber orientation. After 3 h of exposure at 1000 °C, a total weight loss of up to 37% for LCFC and 47% for SMFC could be determined. The bending test carried out after 50 min exposure at 700 °C showed a dramatic decrease down to 50% of the initial flexural strength for LCFC samples with fibers orientated in parallel to the beam axis. The smallest strength decrease of around 13% was found for SMFC samples with fibers orientated perpendicularly to the beam axis. Microstructural investigations suggest strongly that oxidation along the fibers is the most dominating weakening mechanism and is therefore directly affected by the fiber orientation and length.

Effect of fiber type on the mechanical properties of C/C-SiC composites

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

EFFECT OF C/C POROUS PREFORM ON THE MICROSTRUCTURE AND FLEXURAL STRENGTH OF C/C-SiC COMPOSITES

Effects of Carbon Fiber Architecture on the Microstructure and Mechanical Property of C/C-SiC Composites

Effect of Fiber Content on Mechanical Property and Fracture Mechanisms of Cf/SiC Composites

Effect of Pyrocarbon Content in C/C Preforms on Microstructure and Mechanical Properties of the C/C–SiC Composites

Effect of Carbon Particle and Carbon Fiber on the Microstructure and Mechanical Properties of Short Fiber Reinforced Reaction Bonded Silicon Carbide Composite

Effects of needle-punched felt structure on the mechanical properties of carbon/carbon composites

Effect of Fiber Characteristics on Fracture Behavior of C F /sic Composites

Mechanical and tribological properties of C/C–SiC ceramic composites with different preforms

Effects of preform structure on microstructure and mechanical properties of long/short fiber‐coupled C/C–SiC composites

Effects of chopped carbon fiber on the forming, structure and mechanical properties of CCF/SiC composites fabricated by SLS and RMI

Effects of carbon fiber dispersion on bending property of Cf/SiC brake materials

Effect of preform structure on mechanical and thermal properties of SiCf/SiC composites

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

Effects of Random Chopped Fiber on the Flexural Strength and Toughness of Reaction Bonded Silicon Carbide Composite

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

Effects of the fiber surface characteristics on the interfacial microstructure and mechanical properties of the KD SiC fiber reinforced SiC matrix composites

Effect of SiC content on the mechanical behaviour of a three-dimensional needled C/SiC composite

Improved Mechanical Properties of Csf/SiC Composite by Rapid Hot Press Sintering