Abstract:This research explored effect of steam curing on strength, durability and microstructure of concretes with and without mineral admixtures of fly ash (FA) and ground granulated blast furnace slag powder (SL). The two types of C55 strength grade concretes (one is pure cement concrete, another one is concrete, replacing part of cement with 12% FA and 18% SL) were prepared and their compressive strength, chloride diffuse on coefficient and carbonation depth under the standard and steam curing conditions were measured and compared. The phase composition and microstructure of the concretes under the two curing conditions were tested by X-ray diffraction (XRD), scanning electron microscope (SEM) and mercury intrusion porosimeter (MIP). The results show that, on the one hand, compared with standard curing, steam curing is beneficial to the early strength, but not conducive to the later strength development and chloride permeability resistance of both two types of concretes. Furthermore, for the steam cured concrete, the 28d carbonation depth of the forming surface is higher than that of the bottom surface. What's more, steam curing can reduce the carbonization resistance of pure cement concrete and improve the carbonization resistance of concrete mixed with FA and SL. On the other hand, composite mineral admixtures of FA and SL reduce the early strength, the carbonization resistance of concrete cured with standard curing, but improve the later strength, the carbonization resistance and chloride permeability resistance of concrete cured with steam curing. FA and SL are thermally activated under steam curing and can react with the calcium hydroxide formed by cement hydration in the early stage, which produces larger amount of secondary hydration products to improve the pore structure and interfacial microstructure of the concrete with FA and SL. Thus, the adverse effects of steam curing on later strength and durability of concrete are significantly restrained by composite mineral admixtures of FA and SL.

Study on mechanical properties and long term properties of steam-cured fly ash concrete with activating agent

Study on the Effect of Fly Ash and Polycarboxylic Acid Water Reducer on the Properties of Recycled Concrete

Effect of Forepart Strength of Cured-concrete

Experimental study on the activators of fly ash

Effects of compound activators on the early mechanical properties of cement mortar incorporating large volume of fly ash

Influence of expansive agent on the cracking resistance performance of fly ash concrete

Effect of Curing Regime on the Mechanical Properties and Durability of Steam Cured-Concrete

The Effect of Mechanical Activation of Fly Ash on Cement-Based Materials Hydration and Hardened State Properties

Experimental Research on the Using of FJ1-activator in High Strength Concrete with High Content of Fly Ash

Effect of steam curing on strength, durability and microstructure of concretes with and without mineral admixtures

Effect of Curing Conditions on Property of High Performance Concrete with Composite Mineral Admixture

Investigating the Impact of Fly Ash on the Strength and Micro-Structure of Concrete during Steam Curing and Subsequent Stages

Research on Improving Cementitious Material Properties by Adding FineFly Ash

Mechanism of fly ash's effects during hydration process of composite binder

Influence of Calcined Flue Gas Desulfurization Gypsum and Calcium Aluminate on the Strength and AFt Evolution of Fly Ash Blended Concrete under Steam Curing

Strength characteristics of self-compacting concrete with alkali-activated fly ash

Study on Mechanics Property Experiments of High Fly Ash Content Concrete

Strength and Microstructural Characteristics of Activated Fly Ash–Cement Paste

Experimental Study on Effect of Content of Quicklime on Compressive Strength of Low-Calcium Fly Ash Mortar

Influence of High-Volume Mineral Mixtures and the Steam-Curing Temperatures on the Properties of Precast Concrete

The Effect of Changing Fly Ash Content on the Modulus of Compression of Stabilized Soil