Corrosion Fatigue Crack Growth of Marine Steel Under Dry-wet Cyclic Conditions

Bo HONG,Yi HUANG,Zhimin WU
DOI: https://doi.org/10.3969/j.issn.1672-1144.2015.05.027
2015-01-01
Abstract:An investigation was presented on the d a/d N of D36 steel with three-point bending fatigue test under different k .The corrosion fatigue specimens were tested considering the changes in loading frequency f ,as well as dry-wet time ratio k .The experimental results indicate that d a/d N is closely related to k and loading frequency f .When subjected to alternating dry-wet time ratio ,d a/d N shows a trend of first increase and then decrease with the increasing of k in the low stress intensity factor amplitude (Δk ) phase .However ,d a/d N presents negligible dependence on k in the highΔk phase .Changing the loading frequency has an influence on d a/d N which shows that the lower the frequency the faster the cracking rate ,especially in the low Δk phase .