Abstract:The performance of fresh (PdV/TiO2), sulfur poisoned (Used-S and Used-H), and regenerated (Used-RS and Used-RH) multi-active center catalysts for chlorobenzene catalytic oxidation and selective catalytic reduction (CBCO + SCR) reaction is investigated. The reaction on the catalyst surface is blocked after sulfur poisoning owing to the occupation and deposition of catalyst active centers (mainly Pd centers) by PdSO4 (and/or PdS in a dry environment) and NH4HSO4 species, especially the CBCO process. Sulfates (mainly NH4HSO4) on the sulfur poisoned catalyst surface are partially decomposed after 400 °C thermal regeneration, while the deactivation caused by the formation of PdSO4 species is irreversible. Density functional theory calculation results show that in the PdSO4 and NH4HSO4 generation paths, each step of the elementary reaction has just a small energy barrier to overcome, and the stability of the product for each elementary reaction increases gradually. Even worse, SO2 is easily combined with H2O gas molecules to form H2SO3 in a humid environment, and the energy barrier for conversion of SO32– to SO42– is just 0.041 eV. The two oxygen vacancies (VOx-1 or TiOx-1) provide adsorption sites for CBCO + SCR reaction gas molecules but do not exhibit adsorption properties for SO2, which gives a possible idea for optimization of sulfur resistance. The present work is favorable for further synergistic removal of CB/NOx by the catalyst for anti-SO2 poisoning modification and application in the manufacture industry.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.est.1c03617.Details of the Section 2 in this work; reaction condition information, general properties, gaseous reaction byproducts, and Raman analysis; HRTEM image and pyridine-IR profile (Figure S1); basic information of the Pd0.12V4/TiO2 catalyst (Table S1); CB TOF (Table S2); NO TOF (Table S3); effect of 600 ppm SO2 on CB/NO conversion and CO2/N2 selectivity (Figure S2); CB oxidation products (Table S4); gaseous compounds (Figure S3); physicochemical properties of catalysts (Table S5); SEM-EDS mapping images (Figure S4); Raman spectra (Figure S5); Ti 2p XPS profiles (Figure S6); H2-TPR profiles (Figure S7); in situ DRIFT spectra (Figure S8); corresponding species for in situ DRIFT spectra peaks (Table S6); optimized multi-active center catalyst structure (Figure S9); dehydrogenation path for H2O (Figure S10); coadsorption configurations and PDOS of SO2 with NO, NO2, O2, NH3, and H2O gas molecules (Figure S11); adsorption energy and bond information of SO2 with NO, NO2, O2, NH3, and H2O (Table S7); competitive adsorption of CB and SO2 (Figure S12); adsorption configuration and PDOS of NO, NH3, and CB on O vacancies (Figure S13); removal path and energy barrier of CB (Figure S14); configurations and PDOS for SO2 on O vacancies (Figure S15); oxidation path of PdSO4 by NO2 (Figure S16); and generation path of NH4SO4ads (Figure S17) (PDF)This article has not yet been cited by other publications.

SO2 Poisoning Mechanism over TiO2-ZrO2 Based Catalyst for Selective Catalytic Reduction of NOx by NH3

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

New Insight into the in Situ SO2 Poisoning Mechanism over Cu-SSZ-13 for the Selective Catalytic Reduction of NOx with NH3

Prominent difference in the deactivation rate and mechanism of V2O5/TiO2 under H2S or SO2 during selective catalytic reduction of NOx with NH3

In situ DRIFTS and DFT studies of SO2 poisoning over Cu-exchanged X zeolite catalyst for NH3-SCR

Deactivation Mechanism of Arsenic and Resistance Effect of SO42− on Commercial Catalysts for Selective Catalytic Reduction of NO with NH3

SO2 Poisoning Behaviors of Ca-Mn/TiO2 Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Support promotion effect on the SO2 and K+ co-poisoning resistance of MnO2/TiO2 for NH3-SCR of NO

Study on SO 2 Poisoning and Regeneration of the Low-Temperature Fe–Sn–Mn/TiO 2 Catalyst for Simultaneous Removal of NO x and Mercury

Insight into SO2 poisoning and regeneration of one-pot synthesized Cu-SSZ-13 catalyst for selective reduction of NO by NH3

Exploring the Role of V2O5 in the Reactivity of NH4HSO4 with NO on V2O5/TiO2 SCR Catalysts

Effect of Various Acid Anions on Potassium Poisoning and the Mechanism of Commercial V 2 O 5 –WO 3 /TiO 2 Catalysts for SCR of NO x

Mechanistic Investigation of the Enhanced SO2 Resistance of Co-modified MnOx Catalyst for the Selective Catalytic Reduction of NOx by NH3

DRIFT Study of the SO<sub>2</sub>Effect on Low-Temperature SCR Reaction over Fe−Mn/TiO<sub>2</sub>

Effects of H2O and SO2 on the Performance of V2O5/TiO2 Catalysts for Selective Catalytic Reduction of NO in Flue Gas

Enhanced Catalytic Performance of V2O5–WO3/Fe2O3/TiO2microspheres for Selective Catalytic Reduction of NO by NH3

Selective catalytic reduction of NO by NH3 over CuO–CeO2 in the presence of SO2

SO 2 Poisoning Mechanism of the Multi-active Center Catalyst for Chlorobenzene and NO x Synergistic Degradation at Dry and Humid Environments

Unraveling the Unexpected Offset Effects of Cd and SO2 Deactivation over CeO2-WO3/TiO2 Catalysts for NOx Reduction

Boosting SO2-Resistant NOx Reduction by Modulating Electronic Interaction of Short-Range Fe-O Coordination over Fe2O3/TiO2 Catalysts

Activity enhancement of sulphated Fe<sub>2</sub>O<sub>3</sub> supported on TiO<sub>2</sub> -ZrO<sub>2</sub> for the selective catalytic reduction of NO by NH<sub>3</sub>