Abstract:Abstract With the continuous improvement of the mechanical properties of composite materials, the adhesive interface performance of composite T-stiffened panels has become a critical factor in determining the overall structural strength. However, little work has been reported on the mechanical properties of adhesive interfaces in composite T-stiffened panels under lateral bending and shear loading. Especially, there is no clear explanation on the damage evolution law of structural properties for the interface with defects, which greatly influenced the use of T-stiffened composite structures. In this paper, the mechanical properties of T1100/5405 composite T-stiffened laminates under lateral bending and shear loading are experimentally and numerically investigated. The load-bearing capacities for the panels with intact and defected adhesive interfaces are compared, the damage evolution law of typical T-stiffened structures is further explored. Based on the continuum damage model (CDM) and the cohesive zone model (CZM), the constitutive models of the adhesive layer and the composite material are established respectively. Good agreements between experimental and numerical profiles illustrate that damages mainly occur on the loading side and the corner of the L-type ribs under lateral bending conditions, while damages extend from both sides of the interface layer to the center under shear loading. When a prefabricated defect exists, damages extend from the defect location along the loading direction. At the same time, the analysis shows that the lay-up of the surface layer, the chamfer radius, and the width of T-type ribs have a great influence on the structural load-bearing capacity, but less on the damage evolution form.

Cohesive zone model for prepreg tack based on probe test

Analysis and Characterization of Interlaminar Tack for Different Prepreg Materials During Automated Fiber Placement

A Novel Model of Z-pin Insertion in Prepreg Based on Fracture Mechanics

Computational modelling of postbuckling behavior of composite T-stiffened panels with different bonding methods

Strengthening of Composite T-joints Using Ø 0.11 Mm Z-pins Via an Ultrasound-Guided Insertion Process

A Peel Test Method to Characterize the Decay Law of Prepreg Tape Tack at Different Temperatures

Influence and optimization of parameters of prepreg viscosity during placement

Analysis and modeling of the Z‐pin insertion in prepreg based on contact mechanism

Hot-press bonding mechanism and mechanism designing for prepreg

Characterization of Inter-Ply Slipping Behaviors in Hot Diaphragm Preforming: Experiments and Modelling

Understanding the compaction behavior of uncured thermoset prepreg: Experimental investigation and theoretical analyses

Interply friction of carbon fiber/epoxy prepreg stacks under different processing conditions

Cohesive zone modeling for viscoplastic behavior at finite deformations

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Effect of Temperature on Probe Tack Adhesion: Extension of the Dahlquist Criterion of Tack

Preparation of Z-Pin from Different Resin and Evaluation of Inter Laminar Reinforcement Effect by Pullout Test

The effects of environments and adhesive layer thickness on the failure modes of composite material bonded joints

Research on Placement Techniques of Epoxy Matrix Composite Prepreg

Investigation of the out-of-plane load-bearing capacity of T1100/5405 composite T-stiffened panels

Preparation Process of Continuous CF Reinforced PEEK Composite Laminates

Study on impregnation parameters in preparation of CFF/PEEK laminates