Numerical Analysis of Stress and Strain in a Service-work-hardened High Manganese Steel Crossi ng Nose

MA Peng-hui,QIAN Li-he,ZHANG Han-lin,LIU Shuai,ZHANG Fu-cheng

DOI: https://doi.org/10.3969/j.issn.1001-8360.2015.02.013

2015-01-01

Abstract:A three dimensional elastic‐plastic finite element model consisting of a railway crossing and a train wheel was established to investigate the stress/strain field in a high manganese steel crossing nose . Two serv‐ice states of the crossing at a nose width of 50 mm were considered in the paper ,i.e.non‐work hardening cor‐responding to the early service stage and work hardening corresponding to the later service stage ,and the in‐fluence of service work hardening on the magnitude and distribution of stress/strain in the crossing nose was analyzed .In the case of simulation of service work hardening ,a layered model was constructed and various material properties were assigned to corresponding layers ,according to the effect of the distance from the sur‐face of an actual work‐hardened crossing nose on the material properties ,while a homogeneous material prop‐erty was assigned to the entire model with non‐work hardening . The results indicate that ,during both the ear‐ly and later service stages , the von Mises stress and equivalent plastic strain rapidly increase and then gradually decrease with the increase of the depth . As compared with the early service stage , during the later service stage ,the maximum von Mises stress of the crossing nose increased by about 23% ,while the maximum equiv‐alent plastic strain decreased by about 40% ,and the plastic strain zone reduced significantly . The reason for this is due to the largely increased yield strength of the crossing nose after service work hardening .It is there‐ <br> fore believed that the surface quashing and the formation of overlap in the crossing nose may be largely sup‐pressed owing to the service work hardening . Furthermore , as compared to the non‐work‐hardened crossing nose , the distance between the location of the maximum equivalent plastic strain of the work‐hardened crossing nose and the surface of the crossing nose increases from 0.8 mm to 1.5 mm ,indicating that crack initiation site tends to move to locations farther away from the crossing nose surface .