Numerical Analysis on Prediction of Rolling Contact Fatigue Crack Initiation Life of Wheel

YU Rong-quan,LI Qiang,LI Na,ZHENG Jing

DOI: https://doi.org/10.3969/j.issn.1001-8360.2015.12.004

2015-01-01

Abstract:A 2-D finite element model of the wheel with a defect hole was established by finite element software ABAQUS.The Lemaitre-Chaboche nonlinear isotropic/kinematic hardening cyclic plastic model was used for the cyclic plastic constitutive relation to simulate the repeated rolling contact of the wheel through the moving normal distribution pressure and tangential distribution force applied on the rolling contact surface .The Jiang-Sehitoglu damage parameters and the critical plane approach based fatigue crack initiation life model were used to analyze the influence of the factors such as cyclic loading,the depth of defect hole and friction factor on the damage parameters of wheel defect hole and the rolling contact fatigue crack initiation life .The results showed that after repeated cyclic loading for ten times,the stress and strain response of the defect hole of the wheel material gradually stabilized .The effects of the factors such as cyclic loading,the depth of the defect hole and the friction factor on the damage parameters of the wheel defect hole and the rolling contact fatigue crack initia-tion life of the wheel were obvious .The fatigue crack initiation life increased with the increase of the cyclic load and friction factor while decreased with the increase of the depth of the defect hole .