High-Quality All-Inorganic Perovskite CsPbBr 3 Microsheet Crystals as Low-Loss Subwavelength Exciton–Polariton Waveguides

Zijuan Li,Fengsheng Sun,Zebo Zheng,Jun Chen,Albert V. Davydov,Shaozhi Deng,Huairuo Zhang,Huanjun Chen,Fei Liu

DOI: https://doi.org/10.1021/acs.nanolett.0c04908

IF: 10.8

2021-02-09

Nano Letters

Abstract:Nanostructured all-inorganic metal halide perovskites have attracted considerable attention due to their outstanding photonic and optoelectronic properties. Particularly, they can exhibit room-temperature exciton–polaritons (EPs) capable of confining electromagnetic fields down to the subwavelength scale, enabling efficient light harvesting and guiding. However, a real-space nanoimaging study of the EPs in perovskite crystals is still absent. Additionally, few studies focused on the ambient-pressure and reliable fabrication of large-area CsPbBr₃ microsheets. Here, CsPbBr₃ orthorhombic microsheet single crystals were successfully synthesized under ambient pressure. Their EPs were examined using a real-space nanoimaging technique, which reveal EP waveguide modes spanning the visible to near-infrared spectral region. The EPs exhibit a sufficient long propagation length of over 16 μm and a very low propagation loss of less than 0.072 dB·μm^–1. These results demonstrate the potential applications of CsPbBr₃ microsheets as subwavelength waveguides in integrated optics.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.nanolett.0c04908?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.nanolett.0c04908</a>.Table S1, Table S2; methods; solutions of transverse magnetic (TM) and transverse electric (TE) waveguide modes; characterizations of the CsPbBr₃ microsheets (Figure S1); typical XRD pattern of the CsPbBr₃ microsheets (Figure S2); dynamics of the PL of the CsPbBr₃ microsheets (Figure S3); thickness-dependent dispersion relations for the TE and TM modes of the CsPbBr₃ microsheet waveguide (Figure S4); additional s-SNOM analyses of the CsPbBr₃ microsheets (Figure S5); s-SNOM images demodulated at different harmonics (Figure S6) (<a class="ext-link" href="/doi/suppl/10.1021/acs.nanolett.0c04908/suppl_file/nl0c04908_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology