Lasing from solution-processed CsPbBr3 octahedral resonators

Xun Sun,Zhenhua Gao,Weiguang Zhang,Yang Liu,Baoyuan Xu,Zifei Wang,Xue Wang,Xiangeng Meng

DOI: https://doi.org/10.1016/j.jlumin.2020.117713

IF: 3.6

2021-01-01

Journal of Luminescence

Abstract:<p>CsPbBr₃ has been recognized as one of the most important members in the family of metal halide perovskites, which could offer high optical gain for low-threshold lasing. Despite of significant advances achieved thus far, it is still in high demand to develop new material platforms to further rationally design perovskite-based resonators. Here, CsPbBr₃ microcrystals in octahedral shape are developed via a simple antisolvent approach, which exhibit single-or dual-mode lasing upon excitation with picosecond laser pulses. The experimental results reveal an unusual phenomenon that the pump threshold shows a profound dropdown of nearly one order from 65.5 down to 7.4 μJ/cm² when the microcrystal size is varying from 20 to 4 μm. The experimental results are in contrary to numerical simulations that a larger microcrystal supports eigenmodes with a higher quality factor. We propose that such a dependence is perhaps dominated with scattering losses of different-sized microcrystals. The lowest pump threshold achieved in CsPbBr₃ octahedral resonators is comparable to those supported in high-quality CsPbBr₃ resonators reported before. The results suggest the potential of the developed CsPbBr₃ octahedral microcrystals in creating high-quality light emitters.</p>

optics

What problem does this paper attempt to address?

This paper aims to explore the performance of CsPbBr₃ octahedral microcrystals prepared by the solution method as laser resonators, especially to study how the size of these microcrystals affects their laser thresholds. The authors found that as the microcrystal size decreased from 20 μm to 4 μm, the pumping threshold decreased significantly by nearly an order of magnitude, from 65.5 μJ/cm² to 7.4 μJ/cm². This result contradicts the prediction of numerical simulations that large - size microcrystals have a higher quality factor (Q - value). The authors propose that this difference may be related to the scattering losses of microcrystals of different sizes, that is, larger microcrystals have higher scattering losses due to increased surface roughness, resulting in a higher pumping threshold.

In addition, the paper also discusses the photostability of these CsPbBr₃ octahedral microcrystals at a low pumping threshold and points out their potential application value, especially in the development of high - efficiency light - emitting devices. The research results show that CsPbBr₃ octahedral microcrystals synthesized by the solution method can be used as high - quality optical resonators to achieve low - threshold laser emission.