Construction of Porous Double Shells in Core-Shell Type Heterojunction Nanostructures As High-Performance Sensing Materials for Gas Detecting
Jinyuan Zhou,Shi Kun Wang,Ao Chen Wang,Chao Yue Zhang,Qian Yu Liu,Jun Di Cheng,Yan Chun Wang,Xiu Ping Gao,Gengzhi Sun,Zhen Xing Zhang,Xiao Jun Pan
DOI: https://doi.org/10.2139/ssrn.4128821
2022-01-01
Abstract:Core-shell heterojunction nanostructures have been often synthesized and applied as gas sensing materials due to their advantages in enhancing sensing response, selectivity, and response/recovery rate. However, the core materials are often greatly limited in the synergistic enhancement for gas sensing performances due to the blocking effect from the shell materials. Here, a type of core-double-shell nanotubes of β-In2S3/In2O3/β-In2S3 (ISOS CDSNTs) was designed via the traditional electrospinning technique combining with a post vulcanization process. In this design, the ISOS CDSNTs possess double β-In2S3/In2O3 heterojunctions at both sides of In2O3 tube wall, and the β-In2S3 shells are particle-filled and porous, which often makes the target gas easily diffuse through the shell layers to the cores. As a result, to 100 ppm ethanol at work temperature of 200 ºC, the ISOS CDSNT sensors show a 76%-improved response compared to that of the In2O3 NT ones. Moreover, the CDSNT sensors also exhibit a fast response/recovery rate and good gas selectivity. The analysis results indicate that the enhanced sensor performance is attributed to the formation of heterojunctions and synergistic effect of β-In2S3 and In2O3. Furthermore, series of tests and analysis indicate that this improved response could be mainly due to the large increase in the resistance in air (Ra) that caused by the double β-In2S3/In2O3 heterojunctions and the increased oxygen vacancies, the accelerated response/recovery rate could be mainly due to the double constructed heterojunction, and the improved gas selectivity could be mainly due to the β-In2S3 shell.