Abstract:Low-quality silicon such as upgraded metallurgical-grade (UMG) silicon promises to reduce the material requirements for high-performance cost-effective photovoltaics. So far, however, UMG silicon currently exhibits the short diffusion length and serious charge recombination associated with high impurity levels, which hinders the performance of solar cells. Here, we used a metal-assisted chemical etching (MACE) method to partially upgrade the UMG silicon surface. The silicon was etched into a nanostructured one by the MACE process, associated with removing impurities on the surface. Meanwhile, nanostructured forms of UMG silicon can benefit improved light harvesting with thin substrates, which can relax the requirement of material purity for high photovoltaic performance. In order to suppress the large surface recombination due to increased surface area of nanostructured UMG silicon, a post chemical treatment was used to decrease the surface area. A solution-processed conjugated polymer of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) was deposited on UMG silicon at low temperature (&lt;150 °C) to form a heterojunction to avoid any impurity diffusion in the silicon substrate. By optimizing the thickness of silicon and suppressing the charge recombination at the interface between thin UMG silicon/PEDOT:PSS, we are able to achieve 12.0%-efficient organic-inorganic hybrid solar cells, which are higher than analogous UMG silicon devices. We show that the modified UMG silicon surface can increase the minority carrier lifetime because of reduced impurity and surface area. Our results suggest a design rule for an efficient silicon solar cell with low-quality silicon absorbers.

High Efficiency Organic/silicon Hybrid Solar Cells with Doping-Free Selective Emitter Structure Induced by a WO3 Thin Interlayer

Highly Efficient Organic/Silicon Hybrid Solar Cells with a MoO3 Capping Layer

High-Efficiency Silicon/Organic Heterojunction Solar Cells with Improved Junction Quality and Interface Passivation

Phosphorus and Selenium Co‐Doped WO3 Nanoparticles for Interface Modification and Photovoltaic Properties Enhancement of Monolayer Planar Silicon/PEDOT:PSS Hybrid Solar Cells

Over 16% Efficiency Organic/nanostructured Si Heterojunction Solar Cells with a P-Doped Organic Small Molecule Layer

High Efficiency Organic/Silicon-Nanowire Hybrid Solar Cells: Significance of Strong Inversion Layer

Improving the Organic/Si Heterojunction Hybrid Solar Cell Property by Optimizing Pedot:Pss Film and with Amorphous Silicon As Back Surface Field

High-performance Si/organic Hybrid Solar Cells Using a Novel Cone-Shaped Si Nanoholes Structures and Back Surface Passivation Layer

Improving Performance of Organic-Silicon Heterojunction Solar Cells Based on Textured Surface Via Acid Processing

Over 16.7% Efficiency Organic‐Silicon Heterojunction Solar Cells with Solution‐Processed Dopant‐Free Contacts for Both Polarities

High-Efficiency Si-Organic Hybrid Solar Cells Using Au@Mos2 Doped Pedot:Pss

Realization of 13.6% Efficiency on 20 μm Thick Si/Organic Hybrid Heterojunction Solar Cells via Advanced Nanotexturing and Surface Recombination Suppression

High-Performance Ultrathin Organic-Inorganic Hybrid Silicon Solar Cells via Solution-Processed Interface Modification.

Boost Organic‐Silicon Hybrid Solar Cell Performances with a Facile and Cost‐effective Sub‐3 nm Interface Control Method

A 12%-efficient upgraded metallurgical grade silicon-organic heterojunction solar cell achieved by a self-purifying process.

Highly Efficient Organic Solar Cells Enabled by the Incorporation of a Sulfonated Graphene Doped PEDOT:PSS Interlayer

High Performance Organic/20μm Crystalline-Silicon Heterojunction Solar Cells

Structural Design and Simple Posttreatment of the Hole Transport Layer to Improve Performance of Hybrid Solar Cells

Solution‐Processed Organic/p‐Type Silicon Hybrid Heterojunction Solar Cells

Fabrication of an Organic/Inorganic Silicon Hybrid Solar Cell Based on PEDOT:PSS Doped and Non-Doped with CBP and Dibenzothiopene-Benzoyl-Tertiarybutylcarbozole

16% Efficient Silicon/organic Heterojunction Solar Cells Using Narrow Band-Gap Conjugated Polyelectrolytes Based Low Resistance Electron-Selective Contacts