Flow stress prediction of Hastelloy C-276 alloy using modified Zerilli−Armstrong, Johnson−Cook and Arrhenius-type constitutive models
LIU Yu,LI Ming,Xian-wei REN,Zheng-bing XIAO,Xie-yi ZHANG,Yuan-chun HUANG,Yu LIU,Ming LI
DOI: https://doi.org/10.1016/s1003-6326(20)65440-1
IF: 3.752
2020-11-01
Transactions of Nonferrous Metals Society of China
Abstract:To better understand the hot deformation behaviors of Hastelloy C-276 alloy under elevated temperatures, hot tensile tests were carried out in the temperature range of 1223−1423 K and the strain rate range of 0.01−10 s<sup>−1</sup>, respectively. Based on the modified Zerilli−Armstrong, modified Johnson-Cook, and strain-compensated Arrhenius-type models, three constitutive equations were established to describe the high-temperature flow stress of this alloy. Meanwhile, the predictability of the obtained models was evaluated by the calculation of correlation coefficients (<em>r</em>) and absolute errors (<em>Δ</em>), where the values of <em>r</em> for the modified Zerilli−Armstrong, Johnson−Cook, and Arrhenius-type constitutive models were computed to be 0.935, 0.968 and 0.984, and the values of <em>Δ</em> were calculated to be 13.4%, 10.5% and 6.7%, respectively. Moreover, the experimental and predicted flow stresses were compared in the strain range of 0.1−0.5, the results further indicated that the obtained modified Arrhenius-type model possessed better predictability on hot flow behavior of Hastelloy C-276.
metallurgy & metallurgical engineering