The Simulation and Experiment Research on Contact Fatigue Performance of Acetal Gears

Zehua Lu,Huaiju Liu,Renhua Zhang,Caichao Zhu,Yaqiang Shen,Dong Xin
DOI: https://doi.org/10.1016/j.mechmat.2020.103719
IF: 4.137
2020-01-01
Mechanics of Materials
Abstract:Acetal gears are the most widely applied type among these polymer gears. Acetal gears may suffer from many failure forms such as severe wear, tooth breakage or tooth surface cracks depending on the loading conditions and the lubrication and temperature environment. The contact fatigue performance of acetal gear relates to many factors including temperature and load, however, their influences on the mechanical properties and fatigue parameters of the acetal material are still not fully understood. In this work, the thermo-elastic-plastic constitutive equations are derived to describe the acetal material behavior during gear meshing process, and the modified Brown-Miller multi-axial fatigue criterion is proposed to estimate the polymer gear contact fatigue life. Durability tests of acetal gear against steel gear are conducted based upon a developed test rig. Results reveal that the temperature rise could significantly reduce the contact pressure of acetal gear due to the decay of the modulus, but still jeopardize the fatigue life on tooth flank because the fatigue properties are also affected by the temperature rise. The predicted location of fatigue failure zone on the tooth and the lifespan agree well with experimental observation.
What problem does this paper attempt to address?