Abstract:Highlights • The high rolling temperature would impede the DRX occurrence for these final-rolled sheets. • The reduction of the volume fraction of this β phases led to the highest peak-aging hardness in R-450 °C sheet. • The precipitate chains in R-385 °C + A sheets were beneficial for strength and elongation. • The traditional precipitation characteristic in R-450 °C + A sheet was bad for elongation but good for strength. • The peak-aging R-450 °C sheet showed the highest strength, i.e. UTS of 518±17 MPa and YS of 438±18 MPa. In this investigation, a high-strength Mg-12Gd-1.0Er-0.5Zr (wt.%) alloy sheet was produced by hot extrusion (HE) and subsequent hard-plate rolling (HPR) at different temperatures. The results indicate that the microstructures of these final-rolled sheets are inhomogeneous, mainly including coarse deformed grains and dynamic recrystallized (DRXed) grains, and the volume fraction of these coarse deformed grains increases as the rolling temperature increases. Thus, more DRXed grains can be found in R-385 °C sheet, resulting in a smaller average grain size and weaker basal texture, while the biggest grains and the highest strong basal texture are present in R-450 °C sheet. Amounts of dynamic precipitation of β phases which are mainly determined by the rolling temperature are present in these sheets, and its precipitation can consume the content of Gd solutes in the matrix. As a result, the lowest number density of β phase in R-450 °C sheet is beneficial to modify the age hardening response. Thus, the R-450 °C sheet displays the best age hardening response because of a severe traditional precipitation of β' (more) and β Η / β Μ (less) precipitates, resulting in a sharp improvement in strength, i.e. ultimate tensile strength (UTS) of ∼ 518 ± 17 MPa and yield strength (YS) of ∼ 438±18 MPa. However, the elongation (EL) of this sheet reduces greatly, and its value is ∼ 2.7 ± 0.3%. By contrasting, the EL of the peak-aging R-385 °C sheet keeps better, changing from ∼ 4.9 ± 1.2% to ∼ 4.8 ± 1.4% due to a novel dislocation-induced chain-like precipitate which is helpful to keep good balance between strength and ductility.

Development of the Fine-Grained Mg-0.6Zr Sheets with Enhanced Damping Capacity by High Strain Rate Rolling

Dynamic recrystallization, texture and mechanical properties of high Mg content Al–Mg alloy deformed by high strain rate rolling

Microstructure, texture evolution and mechanical anisotropy of Mg-Gd-Y-Zn-Zr alloy sheets produced by unidirectional and cross rolling

Enhanced Mechanical Properties of Extruded Mg–Y–Zn Alloy Fabricated Via Low-Strain Rolling

Dynamic precipitation and twinning-induced dynamic recrystallization in Mg–6Al–3Sn–1Zn alloy during multi-pass high-speed rolling

Effects of Annealing Treatment on Mechanical and Damping Properties of ZK60 Magnesium Alloy Sheets

Microstructure and mechanical property of multi-pass low-strain rolled Mg-Al-Zn-Mn alloy sheet

Microstructure, texture and mechanical properties of the rolled high modulus Mg-Y-Zn-Al-Li alloy

Microstructure, mechanical properties and damping behavior of novel Mg-Ga-Zn alloys fabricated by medium-high strain rate rolling

Effects of deformation temperatures on microstructures, aging behaviors and mechanical properties of Mg-Gd-Er-Zr alloys fabricated by hard-plate rolling

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Influence of Microstructure and Mechanical Properties on Formability in High Strain Rate Rolled AZ31 Magnesium Alloy Sheets

Effect of cold rolling on microstructure and mechanical properties of pure Zr

Formation Mechanism of Surface Gradient Microstructure and Mechanical Properties Evolution of Mg-Y-Nd-Gd-Zr Alloy by Ultrasonic Rolling

Achieving high damping and excellent ductility of Al Mg alloy sheet by the coupling effect of Mg content and fine grain structure

An ultrahigh strain-independent damping capacity in Mg–1Mn alloy by cold rolling process

Friction-mediated tuning of shear deformation and microstructure in asymmetrically rolled Mg–1Gd alloy strips

Influence of Processing Temperature and Strain Rate on the Microstructure and Mechanical Properties of Magnesium Alloys Processed by Single-Pass Differential Speed Rolling

Microstructures and mechanical properties of Mg-15Gd-1Zn-0.4Zr alloys treated by ultrasonic surface rolling process

Effect of ultrasonic surface rolling process on microstructure and properties of rolled Mg-Y-Nd-Zr alloy

Microstructure characteristics, yield asymmetry and fracture mechanism of the fine grained thin-wall Mg-6.03Zn-0.55Zr tubes fabricated by hot spinning