Abstract:CaCu3Ti4O12 (CCTO) ceramics have drawn much attention for their potential application in energy storage components and overvoltage protection devices. In order to improve the electrical properties and understand the colossal dielectric behavior, several CCTO ceramic samples were prepared and heat treated in different atmospheres. The results showed that the breakdown field and nonlinear coefficient were effectively intensified, and the dielectric loss was reduced after heat treatments in the oxidizing atmosphere including air and oxygen. However, CCTO phases will decompose into TiO2, CuO and CaTiO3 phases when heat treated in the neutral atmosphere such as nitrogen, losing its colossal dielectric behaviors and excellent electrical properties. It was found that the oxygen atmosphere played the most beneficial effect in improving the characteristics of CCTO ceramics in this research. The maximum stored energy density of CCTO can be promoted from 7.7 to 26.5 kJ/m(3), and the barrier height between grain boundaries were increased from 0.46 to 0.62 eV which may be closely related with its high breakdown filed. Three dielectric relaxations were observed in CCTO ceramics. After heat treatment in oxygen atmosphere, the activation energies of the two relaxation peaks (peak 1 and peak 2) in high frequencies kept nearly constant, at 0.11 and 0.51 eV respectively, while the activation energy of relaxation peak 3 at low frequency were enhanced from 0.75 to 0.85 eV, which may be related to the oxygen vacancy defects. Moreover, the contribution of dc conductivity to dielectric loss can be effectively restrained. An equivalent circuit model was proposed according to impedance analysis to expound the correlation between electrical properties and dielectric relaxations.

Dielectric Relaxation Behavior and Mechanism of Y2/3Cu3Ti4O12 Ceramic

Dielectric Relaxation Behavior and Mechanism of Y 2/3 Cu 3 Ti 4 O 12 Ceramic

Structure and Dielectric Relaxations of CaCu3Ti4O12 Ceramics by Heat Treatments in Different Atmospheres

Influence of Interface Point Defect on the Dielectric Properties of Y Doped CaCu3Ti4O12 Ceramics

Study on the Origin of Giant Dielectric Constant of CaCu3Ti4O12 Ceramics

Electric and Dielectric Behaviors of Y-Doped Calcium Copper Titanate: Rapid Communications of the American Ceramic Society

Dielectric properties and relaxation mechanism of CaCu3Ti4O12 ceramics

Dielectric Relaxation in Tb0.5Y0.5MnO3 Ceramics

Analysis of complex impedance and electrical conductivity of YCra<sub>0.</sub><sub>5</sub>Mn<sub>0</sub><sub>.5</sub>O<sub>3</sub>-Ca Cu<sub>3</sub>Ti<sub>4</sub>O<sub>12</sub> negative temperature coefficient ceramics

Incipient Ferroelectricity and Conductivity Relaxations in Dy2Ti2O7

Intrinsic and Extrinsic Relaxation of CaCu3Ti4O12 Ceramics: Effect of Sintering

Oxygen-defects-related dielectric response in CaCu3Ti4O12 ceramics

Effect of Defect Dipoles on the Colossal Dielectric Behaviors of TiO2-x Ceramics

Effect of oxygen sintering atmosphere on the electrical behavior of CCTO ceramics

Dielectric Relaxations of Yttrium Iron Garnet Ceramics over A Broad Temperature Range

Influence of Sintering Atmosphere and Thermobaric Treatment (TBT) on Dielectric Behaviors of CaCu3Ti4O12 Ceramics

Analysis of complex impedance and electrical conductivity of YCr0.5Mn0.5O3–CaCu3Ti4O12 negative temperature coefficient ceramics

Transition of the colossal permittivity related dielectric relaxation in V-doped CaCu<sub>3</sub>Ti<sub>4</sub>O<sub>12</sub> ceramics

Low dielectric loss, colossal permittivity, and high breakdown electric field in Al-doped Y2/3Cu3Ti4O12 ceramics

Polaron relaxation and non-ohmic behavior in CaCu3Ti4O12 ceramics with different cooling methods

Oxygen-Vacancy-Related High-Temperature Dielectric Relaxation In Srtio3 Ceramics