Abstract:The phase equilibrium of Mg-Cu-Ca ternary system at 350 degrees C were investigated using thirteen key samples. Scanning electron microscopy (SEM) equipped with energy-dispersive spectroscope (EDS) was employed to investigate equilibrium relationships and phase compositions in alloy samples. Powder X-ray diffraction (XRD) technique was used to analyze the crystal structures of new found phases. Two unreported ternary phases, P1 and Mg25-xCu75Cax were observed and investigated for the first time. The compound P1 has a narrow solid homogeneity ranged from about Mg25Cu35Ca40 to Mg30Cu30Ca40 (in at. %). The solid solubility limit of the compound Mg25-xCu75Cax was found to be 8.03 <= x(Ca) <= 16.67 with constant value of about 75 at. % Cu at 350 degrees C. The 2q of fourteen diffraction peaks of new phase P1 were determined to be 23.0 degrees, 35.9 degrees, 37.3 degrees, 38.9 degrees, 42 degrees, 44 degrees, 47 degrees, 52.5 degrees, 54 degrees, 56.7 degrees, 62.3 degrees, 66.8 degrees, 68.2 degrees and 75.4 degrees. The 2q of ten diffraction peaks of the new compound Mg25-xCu75Cax were confirmed to be 20.5 degrees, 21.2 degrees, 34.7 degrees, 35.7 degrees, 42.3 degrees, 43.3 degrees, 44.8 degrees, 47.3 degrees, 50.5 degrees and 74.5 degrees. The maximum solid solubility of Ca in the terminal compound MgCu2 was found to be 8.83 at. % at 350 degrees C. Ternary maximum solid solubility of binary terminal compounds Mg2Ca, Mg2Cu, Cu5Ca and CuCa were less than 2 at. %. In addition, eight three-phase equilibrium relationships were determined in the present work. (C) 2019 Elsevier B.V. All rights reserved.

Phase Equilibria of the Al-Ti-Er Ternary System at 500 °C

Isothermal Section of the Al2O3–TiO2–Er2O3 Phase Diagram at 1400°C

Phase equilibria in Ni–Ti–Ta ternary system

Experimental Investigation of Phase Equilibria in the Co-Ta-Si Ternary System

Phase equilibria in Co−Al−Re ternary system at 1100 and 1300 °C

Phase equilibria in Co-Ti-Re ternary system

Phase Equilibria of the Al-Li Binary System

Phase relationships and transformations in the ternary aluminum—titanium—tantalum system

Solidification paths and phase equilibria at 873 and 673 K in the Al-Er-Zr system

Phase Equilibria in the Er-Co, Er-Fe and Er-Co-Fe Systems

PHASE EQUILIBRIA INVESTIGATION OF BINARY, TERNARY, AND HIGHER ORDER SYSTEMS. PART 1. THE PHASE DIAGRAMS OF THE SYSTEMS Ti-Nb-C, Ti-Ta-C, AND Ti-Mo-C

Phase Relationships in the Al-rich Region of the Al-Y-Zr System

Experimental Investigation and Thermodynamic Assessment of Phase Equilibria in the Al-Ta-V Ternary System

Ag-Cu-Te Phase Equilibria Isothermal Sections at 600 °C and 400 °C

Experimental determination of the liquidus projection of the B-Cr-Ti system

Experimental Determination of the Phase Equilibrium in the Mg–Cu–Ca Ternary System at 350 °C

Quantitative Phase Analysis In The Ti-Al-C Ternary System By X-Ray Diffraction

Phase Diagram of Ternary Co–Fe–Ge System (I): Experimental

Phase Equilibria of the Cu-Se-Te Ternary System

Experimental determination of the phase equilibria of aluminum-rich Al−Li−Cu alloys

Experimental Investigation of Phase Equilibria in the Ti-Cr-V System at 1000–1200 °C