Abstract:Molybdenum disulphide (MoS2) is widely used in tribological applications because of its solid lubricating properties. However, its performance needs to be further improved. In this work, an attempt has been made to improve the tribological performance of MoS2 coating by incorporating TiO2 nanoparticles as a reinforcement material into the MoS2 base matrix. The effects of crystallite size and wt.% addition of TiO2 onto the tribological properties of composite MoS2–TiO2 have been studied. Prior to application of the coating onto the substrate surface, it was pre-treated by phosphating which leads to improvement in the porosity and helps to enhance the bond strength between the coating and steel substrate. A tribological study of composite pure MoS2 coating and MoS2–TiO2 coating was carried out using the pin-on-disc test rig at different operating conditions (contact pressure, speed and temperature). It was observed that composite MoS2–TiO2 coating exhibits excellent tribological properties as compared to pure MoS2 coating. In addition, crystallite size of TiO2 and its different weight% significantly affect the tribological properties of the composite coating. Among all samples of composite MoS2–TiO2 coating, the sample C (27.69 nm crystallite size) with 15% wt. of TiO2 depicts the lowest friction coefficient and wear rate. The influence of temperature and coating thickness on the tribological properties of composite coating has been studied. The frictional coefficient has been reduced, and the wear rate increased with an increase in temperature of the coated pin surface. The similar kind of trend has been observed with respect to the coating thickness.

Tribological Performance of AlCrN–MoS2/PTFE Hard-Lubricant Composite Coatings

Effect of MoS2/PTFE coatings on performance of Si3N4/TiC ceramics in dry sliding against WC/Co

Tribological properties of PEEK-based composite coating prepared by thermal spraying

Tribological property of MoS2-Cr3O4 nanocomposite films prepared by PVD and liquid phase synthesis

High-temperature tribological properties of AlCrN coatings deposited on textured surfaces under dry friction

Microstructure, Friction, And Wear Properties Of Ni-Al2o3-Mos2 Composite Coatings

Preparation and tribological properties of Mo/MoS2-Pb-PbS composite films

Tribological performance of Mn3(PO4)2 coating and PC/MoS2 coating in Rolling–Sliding and pure sliding contacts with gear oil

Study on Wear and Friction Resistance of CrTiAlMoN Coatings Deposited by Magnetron Sputtering

Tribological properties of magnetron sputtered MoS2/metal (Ti, Mo) nanocomposite coatings

Tribological Properties of Bi2S3/MoS2 Composite Coatings Deposited on Biomimetic Leaf Vein Textured Surfaces

Tribological and dry drilling performance of WS2/Cr-AlCrN coatings

Friction and wear behaviour of composite MoS2–TiO2 coating material in dry sliding contact

The synergistic action of Ag and MoS2 on tribological properties of Al2O3/Ag(MoS2) composite coatings

Microstructure, Mechanical and Tribological Properties of CrSiC Coatings Sliding Against SiC and Al2O3 Balls in Water

Tribological performance of the gradient composite TiAlSiN coating with various friction pairs

ANALYSIS OF THE TRIBOLOGICAL PROPERTIES OF TiN/Si3N4 NANOCOMPOSITE COATING IN SLIDING CONTACT WITH CERAMIC, STEEL, AND POLYMER COUNTERPART

Improved tribological properties and corrosion protection of CrN coating by ultrathin composite oxide interlayer

Microstructure, mechanical properties and tribological behaviors of TiAlN-Ag composite coatings by pulsed magnetron sputtering method

Enhanced Mechanical and Tribological Capabilities of a Silicon Aluminum Alloy with an Electroplated Ni–Co–P/Si3N4 Composite Coating