Structural features and optical properties of CeO2-containing borosilicate glass based on spectroscopic analysis

Zhenlin Wang,Laifei Cheng

2014-01-01

Abstract:Borosilicate glasses with composition 63SiO(2)-10B(2)O(3)-3Al(2)O(3)-10Na(2)O-10K(2)O-4BaO doped with 1 and 3 mol% cerium oxide (CeO2) were melted at 1500 degrees C followed by annealing at 550 degrees C after quenching. Spectroscopic analysis of the as-prepared glasses using infrared spectroscopy, Raman spectroscopy and UV-visible spectrometry was performed to study the effects of CeO2 doping on the structure and optical properties of the glass. The vibrational spectra of the glasses reveals appreciable changes in relative intensities as a function of the CeO2 content. The transmission spectra and the derived parameter plots exhibit red-shift of the cut-off wavelength as well as a reduction in the optical band gap and energy gap tail in varying degrees compared to the base glass. These changes indicate structural modifications of glass network and electronic structural variations arising from doping and the polyvalent state of the cerium cation. As a network modifier, cerium in borosilicate glass gives rise to number of nonbridging oxygens resulting in scission of the Si-O network and incomplete conversion of [BO3] to [BO4], whereas elevated cerium concentrations suppress further depolymerization of the Si-O network due to the co-existence of tetravalent and trivalent cerium ions, and hence inhibits fiirther reductions in the optical band gap and energy gap tail. Meanwhile the equilibrium between structural disorder and defect repair stemming from polyvalent cerium is proposed to be responsible for the limited decrement of the energy gap tail.