Abstract:This paper is devoted to the evaluation of the "three-body-abrasion" wear behaviour of (wt.%) 5W-5Mo-5V-10Cr-2.5Ti-Fe (balance) multi-component (C + B)-added alloys in the as-cast condition. The carbon (0.3 wt.%, 0.7 wt.%, 1.1 wt.%) and boron (1.5 wt.%, 2.5 wt.%, 3.5 wt.%) contents were selected using a full factorial (32) design method. The alloys had a near-eutectic (at 1.5 wt.% B) or hyper-eutectic (at 2.5-3.5 wt.% B) structure. The structural micro-constituents were (in different combinations): (a) (W, Mo, and V)-rich borocarbide M2(B,C)5 as the coarse primary prismatoids or as the fibres of a "Chinese-script" eutectic, (b) Ti-rich carboboride M(C,B) with a dispersed equiaxed shape, (c) Cr-rich carboboride M7(C,B)3 as the plates of a "rosette"-like eutectic, and (d) Fe-rich boroncementite (M3(C,B)) as the plates of "coarse-net" and ledeburite eutectics. The metallic matrix was ferrite (at 0.3-1.1 wt.% C and 1.5 wt.% B) and "ferrite + pearlite" or martensite (at 0.7-1.1 wt.% C and 2.5-3.5 wt.% B). The bulk hardness varied from 29 HRC (0.3 wt.% C-1.5 wt.% B) to 53.5 HRC (1.1 wt.% C-3.5 wt.% B). The wear test results were mathematically processed and the regression equation of the wear rate as a function of the carbon and boron contents was derived and analysed. At any carbon content, the lowest wear rate was attributed to the alloy with 1.5 wt.% B. Adding 2.5 wt.% B led to an increase in the wear rate because of the appearance of coarse primary borocarbides (M2(B,C)5), which were prone to chipping and spalling-off under abrasion. At a higher boron content (3.5 wt.%), the wear rate decreased due to the increase in the volume fraction of the eutectic carboborides. The optimal chemical composition was found to be 1.1 wt.% C-1.5 wt.% B with a near-eutectic structure with about 35 vol.% of hard inclusions (M2(B,C)5, M(C,B), M3(C,B), and M7(C,B)3) in total. The effect of carbon and boron on the abrasive behaviour of the multi-component cast alloys with respect to the alloys' structure is discussed, and the mechanism of wear for these alloys is proposed.

WEAR RESISTANT HIGH BORON CAST ALLOY - A REVIEW

High Boron Iron-Based Alloy and Its Modification

Microstructure and mechanical properties of high boron white cast iron

Effect of boron on microstructure evolution and properties of wear-resistant cast Fe–Si–Mn–Cr–B alloy

State of Art on Boron White Cast Iron

Toughness Improvement of Austempered Boron Alloyed High Silicon Ferrous Alloy

A review on the steels, alloys/high entropy alloys, composites and coatings used in high temperature wear applications

Morphology Improvement of Boride in High Boron Wear Resistance Alloy

Recent Progress on Wear‐Resistant Materials: Designs, Properties, and Applications

Effect of Boron and Carbon Content on Microstructure and Properties of High Boron Iron-Based Alloy

Significant Improvement in Wear Resistance of CoCrFeNi High-Entropy Alloy via Boron Doping

Investigations of Abrasive Wear Behaviour of Hybrid High-Boron Multi-Component Alloys: Effect of Boron and Carbon Contents by the Factorial Design Method

Tribological behavior of boronized Fe40Mn20Cr20Ni20 high-entropy alloys in high temperature

Enhancing the mechanical, wear and corrosion behaviour of stir casted aluminium 6061 hybrid composites through the incorporation of boron nitride and aluminium oxide particles

Corrosion Wear of Hypereutectic High Chromium Cast Iron: A Review

Tribological Behavior of High Entropy Alloy Coatings: A Review

Study on A New-Type Wear-Resistant White Cast Iron

Fe-Cr-B-based wear-resistant alloys – A review on microstructure and tribological properties

ON THE RESISTANCE TO ABRASIVE WEAR OF CHROMIUM-MANGANESE ALLOYS IN DIFFERENT ENVIRONMENTS

Wear Resistance and High-Temperature Compression Strength of Fcc CuCoNiCrAl 0.5 Fe Alloy with Boron Addition

A Review of Research on Improving Wear Resistance of Titanium Alloys