Influence of α-Phase Morphology on Mechanical Characteristics, Cycle Oxidation, and Hot Corrosion Behavior of Ti-6Al-3Mo-2Nb-2Zr-2Sn-1.5Cr Alloy
Fathy S. Ahmed,Mohamed A. El-Zomor,Magdy S. Abo Ghazala,Ramadan N. Elshaer
DOI: https://doi.org/10.1007/s13632-022-00884-5
2022-09-01
Metallography, Microstructure, and Analysis
Abstract:The influence of α-phase morphology (equiaxed and lamellar) on the mechanical characteristics, cycle oxidation, and hot corrosion behavior of Ti-6Al-3Mo-2Nb-2Zr-2Sn-1.5Cr (TC21) alloy was investigated. The morphology and distribution of microstructure constituents were characterized by optical microscopy and scanning electron microscopy, while constituent compositions were determined with energy-dispersive spectroscopy. The phases in the oxide scale and corrosion products after different treatments were identified by XRD technique. The initial microstructure consists of equiaxed α-phase and intergranular β-grains. However, after heat treatment, the microstructure changed to lamellar, consisting of large grains of β-phase containing colonies of different orientations. The results showed that the microstructure change from equiaxed to lamellar has a small enhancement on microhardness and wear rate. Surface characterization demonstrates that the β-phase is more resistant to corrosion than the α-phase owing to a higher concentration of Nb, Mo, and Zr. Adhered, compact and thin oxide film was formed and grew in thickness with time during cycle oxidation at 600 °C for 50 h. The weight gain of samples with equiaxed and lamellar microstructures after oxidation was 0.3 and 0.28 mg/cm 2 , respectively, where the variation of weight change was tiny. After NaCl hot corrosion test, the weight loss of samples with equiaxed and lamellar microstructures was 13.2 and 6.4 mg/cm 2 . However, the weight change after hot corrosion with a mixture of NaCl + Na 2 SO 4 salts was − 0.88 and 0.07 mg/cm 2 , respectively. The main corrosion products were rutile TiO 2 , Na 4 O 12 Ti 5 , NaTiS 2 , and Ti 6 O, as well as a small amount of NaCl, as identified by XRD on the corroded surfaces depending on the sprayed salt type.