AES and XPS Analysis on Hydrogen Permeation Barrier Formed by Reaction Between Urea and Zirconium Hydride at High Temperature

Yan Guoqing,Chen Yang,Wu Ming,Peng Jiaqing,Wang Lijun
2016-01-01
Abstract:Hydrogen permeation barriers were prepared by the chemical reaction between urea and zirconium hydride at high temperature. The composition and depth of elements, bond state were analyzed by auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS). AES results indicate that the barrier is mainly composed of carbon, nitrogen, oxygen and zirconium, whose thickness is about 3.4 mu m, including 150 nm of nitrogen and carbon. The atomic concentration of carbon and nitrogen decreases continuously, while the content of oxygen and zirconium increases with longer sputtering time. XPS shows that the barrier contains ZrO2 as well as Zr-OH, Zr-N, C-H and N-H bonds. The mechanism of hydrogen resistance may be that hydrogen is captured by carbon, nitrogen and oxygen to form C-H, N-H and O-H bonds, respectively, when it diffuses from zirconium hydrides. Therefore, the prepared coatings can prevent hydrogen permeation effectively.
What problem does this paper attempt to address?