Effect of Cooling Method on Microstructures and Mechanical Properties of Extruded Mg-4.4Zn-0.3Zr-0.4Y Alloy

Lv Binjiang,Peng Jian,Chu Zhong

2017-01-01

Rare Metal Materials and Engineering

Abstract:Mg-4.4Zn-0.3Zr-0.4Y (wt%) alloy ingots were prepared by two casting processes with different cooling methods: air cooling cast (AC cast) and water cooling cast (WC cast). Then, the two types of Mg-4.4Zn-0.3Zr-0.4Y alloy ingots were extruded under the same condition, and the effect of different cooling methods on microstructure and mechanical properties of the extruded alloy was studied. The results show that the cooling method of melt during cast processing has a great effect on microstructure and mechanical properties of the extruded alloy. Compared with AC cast alloy, the lamellar eutectic structure and dendrite cell size of WC cast alloy are significantly refined, while the formation of W-phase (Mg3Y2Zn3) is suppressed and the volume fraction of I-phase (Mg3YZn6) increases in WC cast alloy. After extrusion deformation, the WC cast Mg-4.4Zn-0.3Zr-0.4Y alloy has finer dynamically recrystallized grains, finer and more uniformly fragmented I-phase particles distributed in the matrix and grain boundaries, weakened {0002} basal texture intensity and increased {10 (1) over bar2} texture intensity compared with those of the extruded AC cast alloy. The yield strength and tensile strength of the extruded WC cast Mg-4.4Zn-0.3Zr-0.4Y alloy reach 297.0 and 327.3 MPa, which are increased by 46.4 and 21.4 MPa, respectively compared with those of the extruded AC cast alloy. The extruded WC cast Mg-4.4Zn-0.3Zr-0.4Y alloy shows an elongation of 14.8%, which is 4.7% improvement compared with that of the extruded AC cast alloy.