Effect of Y on the Microstructure and Mechanical Properties of Mg-2Zn-1Mn Alloy

Chen Rong,Xu Junyao,Zhang Dingfei,Yu Daliang,Feng Jingkai

2019-01-01

Rare Metal Materials and Engineering

Abstract:The microstructure and mechanical response of as-cast and extruded Mg-2Zn-lMn-XY alloys (X=0, 0.8, 2.2, wt%) were investigated by optical microscope (OM), scanning electron microscope (SEM) with X-ray energy dispersive spectrometer (EDS), and X-ray diffractometer (XRD). The results reveal that the addition of Y not only decreases the grain sizes of both as-cast and extruded alloys, but also effectively reduces the basal texture intensity of extruded alloys, which are the two key reasons for the improvement of the strength and ductility of Mg-2Zn-1Mn-XY alloys, simultaneously. The optimized Mg-2Zn-lMn-XY alloy after extrusion exhibits an attractive mechanical performance. Compared with those of the matrix material Mg-2Zn-1Mn, its yield strength increases from 164 MPa to 204 MPa, the ultimate tensile strength increases from 237 MPa to 298 MPa, and the elongation increases from 12% to 18%.