Accurate Test of TA15 Titanium Alloy Hot-Rolled Plate with a Large Size and Middle Thickness

Han Liang,Zhang Hui,Zhang Wangfeng,Wang Yuhui,Yan Mengqi

2017-01-01

Rare Metal Materials and Engineering

Abstract:The residual stress was measured by X-ray diffractometer for large-size and middle-thick TA15 Ti alloy plate. By scanning the (213) plane of TA15 titanium alloy by X-ray diffraction, we observed the changes in peak shape, and used the sin(2)psi method to calculate the residual stress. Residual stresses of some locations on the plate surface had large deviations under the normal diffraction conditions, so that the test results are not reliable. On the basis of the range 30 degrees similar to 85 degrees diffraction scans on samples, it is regarded that big deviation of stress is resulted from the coarse grain. So we proposed that increasing the X-ray irradiating area should be an appropriate way to decrease the deviation of the residual stress. After improvement, the results show that the surface of TA15 titanium alloy plate possesses large compressive stress after hot rolling. The surface residual stress range is from 250 to 450 MPa, and measured deviations are within +/- 50 MPa, which is highly reliable. The further analysis of the formation mechanism was conducted on TA15 plate residual stress, providing a theoretical basis and experimental data to eliminate the residual stress.