Effects of Outside Melt Temperature on Microstructure and Properties of 7075/6061 Bimetallic Composite Materials

Zheng Xiaoping,Jiang Long,Gong Wenyuan,Song Jinying,Tian Yaqiang,Chen Liansheng

2018-01-01

Rare Metal Materials and Engineering

Abstract:The 7075/6061 cladding bimetal composite ingots with a "semi-solid microstructure/dendrite microstructure" distribution characteristic were prepared by solid/liquid metals compound casting. The interfacial morphology and mechanical properties of the ingots with different outside melt temperatures were analyzed. At last, the interface bonding mechanism of the ingot was discussed. The results show that the 7075/6061 cladding bimetal composite ingot has advantageous microstructure distribution and morphology, and has the best compressive strength, while the parameters are the outside melt temperature 760 degrees C, the billet pre-temperature 300 degrees C, holding time 40 min and air cooling. With the increasing of the outside melt temperature, the near-spheroidal alpha-Al solid particles of the semi-solid billets of the inner layer 7075 alloy are coarser and more non-spherical, the remelted area of the semi-solid billet at the bonding interface also increases. Otherwise, as the outside melt temperature increases, an evolution rule of the semi-solid microstructures nearby the bonding interface occurs as follows: near-spheroidal solid particles merging and growing, non-spherical crystal, and dendritic crystal. During the compression mechanical property test at ambient temperature, the samples fracture along 45 degrees angle direction to axis, but not along the bonding interface.