Effects of Processing Parameters on Hot Deformation Behavior and Microstructure Evolution of As-cast AZ31B Magnesium Alloy

Zhu Yanchun,Ma Lifeng,Huang Zhiquan,Qin Jianping,Wang Jianmei

2019-01-01

Rare Metal Materials and Engineering

Abstract:The effects of deformation temperature, strain rate and height reduction on hot deformation behavior and microstructure evolution of as-cast AZ31B magnesium alloy were researched in terms of hot compression tests. The results show that the peak stress decreases with the decreasing strain rate and increasing deformation temperature, and the main nucleation mechanism consists of initial grain boundary bulging nucleation, sub-grain rotation nucleation, twinning induced nucleation as well as continuous recrystallization. Moreover, the deformation temperature is below 400 degrees C, the increase in temperature is beneficial to recrystallization and grain refinement, while above 400 degrees C, grain size increases rapidly. Furthermore, the deformation temperature is equal to or lower than 400 degrees C, the lower strain rate of 0.1 s(-1) is more beneficial to the recrystallized grain refinement, while above 400 degrees C, medium strain rate of 1 s(-1) is more advantageous. In addition, it is found that at higher temperature and lower strain rate, height reduction primarily affects the grain size, and at higher temperature and higher strain rate, height reduction primarily affects the dynamic recrystallization degree.