Varying strain rates and elevated temperatures effects on the mechanical properties of AZ31B magnesium alloy
Raj Kumar,Mohammad Mursaleen,G.A. Harmain
DOI: https://doi.org/10.1177/09544089241271882
2024-08-21
Proceedings of the Institution of Mechanical Engineers Part E Journal of Process Mechanical Engineering
Abstract:Proceedings of the Institution of Mechanical Engineers, Part E: Journal of Process Mechanical Engineering, Ahead of Print. This study investigates the monotonic tensile behavior of magnesium (Mg) alloy AZ31B across a temperature range from ambient (25 °C) to elevated (up to 300 °C) with varying strain rates (SR) (1.5 × 10−2 to 1.5 × 10−4 s−1). Mechanical properties such as ultimate tensile strength (σu), tensile yield strength (σy), strain to failure (εf), plastic anisotropy (r-value), strain rate sensitivity (m) and strain hardening exponent (n) were investigated in this study for these strain rates. As the temperature increased from 25 to 300 °C, the following changes in mechanical properties were observed: the yield strength (σy) decreased by 84.50%, the ultimate tensile strength (σu) decreased by 87%, the modulus of elasticity (E) decreased by 63.0%, and the elongation increased by 72.0%. The reduction factors (RF) were proposed for the above-mentioned mechanical properties for varying temperature ranges. The impact of varying temperatures and strain rates on fracture surfaces was investigated using field emission scanning electron microscopy (FE-SEM). The results revealed the presence of tenacity nets, cleavage patterns, and an increasing number of dimples as temperatures increased.
engineering, mechanical