Microstructure and Properties of Mg-3Zn-1Y-0.6Zr-0.5Ca Bio-magnesium Alloy Extruded at Different Speeds

Zhang Wenxin,Sun Yi,Xu Chunxiang,Zhang Jinshan,Jia Qinggong,Kuan Jun
2019-01-01
Rare Metal Materials and Engineering
Abstract:The Mg-3Zn-1Y-0.6Zr-0.5Ca bio-magnesium alloy was prepared by a conventional casting method. The effects of the microstructures and mechanical properties of alloys extruded at different extrusion speeds (10, 30, 60 and 90 mm/min) were investigated. The results show that the size of dynamic recrystallization grains increases, and the area of non-dynamic recrystallization decreases with the increase of the extrusion speeds. Extrusion speeds affect the morphology and distribution of the precipitation, and thus influence the occurrence of dynamic recrystallization in turn. Texture decreases with the increase of the extrusion speed. As the extrusion speed increases, the ductility of the alloy increases but the tensile strength decreases. The alloys exhibits excellent comprehensive performance, whose tensile strength and elongation are 270 MPa and 19.6%, respectively, when the extrusion speed is 60 mm/min.
What problem does this paper attempt to address?