Abstract:We herein report our investigation into the influence of cold-rolling on the recrystallization texture of the Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy during annealing. The as-received plates were cold-rolled at 25 °C with different reductions of 6, 10, 14, 18, 30, 40, 50 and 70%. All cold-rolled sheets were annealed at 580 °C for 3 h, while 14 and 30% cold-rolled samples were also annealed at 580 °C for 12 h. The microstructures of the annealed samples were characterized by scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). Abnormal grains growth with about 23 μm in size appeared in the samples with 14% reduction and annealed at 580 °C for 3 h, which corresponded to the critical degree of alloy deformation. The texture of the 14% cold-rolled sheet was typical rolling texture <0001>//ND, after annealing, cold rolling texture was still retained. While the texture of the 30% cold-rolled sheet was <112¯0> parallel to the rolling direction (<112¯0>//RD), which changed to the recrystallization texture <0001>//ND, <101¯0>//RD and <112¯0>//RD characteristics after annealing. The loading direction is along the rolling direction (RD), the slip system and the Schmid factor are analyzed to more deeply understand and evaluate the plasticity of further rolling or punching. When the loading direction is along the rolling direction (RD), the predominant slip systems of annealed 14% reduction samples was prismatic and pyramidal plane system, and the annealed 30% reduction samples were prismatic with a pyramidal plane system. This implies that the use of 30% cold-rolled reduction and annealing at 580 °C for 12 h imparts a superior plasticity to the alloy, which may allow its application in future deformations, such as rolling or punching.

Evolution of Crystallographic Texture of Zirconium Alloy During Hot Deformation

Deformation Mechanisms and Dynamic Recrystallisation of Zr Alloy with Different Initial Textures Compressed at 700°C

Effect of initial orientation on dynamic recrystallization of a zirconium alloy during hot deformation

Texture Evolution and Dynamic Recrystallization of Zr–1Sn–0.3Nb–0.3Fe–0.1Cr Alloy During Hot Rolling

Dynamic Recrystallization of Zr-1Sn-0.3Nb Alloy During Hot Compression

Effect of Loading Direction on the Deformation and Annealing Behavior of a Zirconium Alloy

Texture and Twinning Evolution of Cold-Rolled Industrial Pure Zirconium

Microstructure and Texture Evolution in Commercial-Purity Zr 702 During Cold Rolling and Annealing

Dynamic Recrystallization and Deformation Model of Β-Quenched Zr-4 Alloy Subjected to Elevated Temperature Compression

Texture Evolution During Isothermal Compression Process of Ti-22Al-25Nb Alloy in B2 Phase Region

Compression Deformation Behavior Of Zr-1sn-0.3nb Alloy With Different Initial Orientations At 650 Degrees C

Investigation on deformation mechanisms of Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy using in situ EBSD/SEM

Texture Evolution of Cold-Rolled Zr-1Sn-0.3Nb-0.3Fe-0.1Cr Alloy During Annealing

Effect of Hot Working Parameters on Microstructure and Texture Evolution of Hot-Deformed Zr-45Ti-5Al-3V Alloy

Mechanism of Crystallographic Orientation and Texture Evolution of Ti60 Alloy during Plane Strain Compression

Texture and Tensile Properties of Zr-Sn-Nb Alloy

Slip Deformation Mechanism of Α-Zr at 700 °C

Texture Analysis of Cu-Cr-Zr Alloy in Process of Deformation

Texture Evolution and Mechanical Anisotropy of Cold-Rolled Zr-4 Alloy Tube after Recrystallization Annealing

Texture Weakening and Grain Refinement Behavior of the Extruded Mg-6.03Zn-0.55Zr Alloy During Hot Plane Strain Compression

Microstructure and texture of coarse-grained Mg-Gd-Y-Nd-Zr alloy after hot compression