Preparation of Hexagonal Wo3 Nanowires and Nh3 Sensing Characteristics

Xu Yuxing,Tang Zilong,Zhang Zhongtai

2009-01-01

Rare Metal Materials and Engineering

Abstract:Hexagonal tungsten oxide nanowires were prepared by a simple hydrothermal method. The diameter of the nanowires is about 10 similar to 20 nm, the length is up to several micrometers and the specific area is 130.69 m(2)/g. Thick film gas sensor was prepared by screen-printing technology and sintered at 350 degrees C for 1 h. The NH3 sensing properties and sensing mechanics at low concentrations (1-100 mu L/L) were investigated in the temperature range from 200 to 350 degrees C. It shows a high sensitivities (R-a/R-g) (4.0-18.8), good repeatability and stability. The sensitivity increased with increasing the operating temperature from 200 degrees C to 350 degrees C for the same NH3 concentration. At the same temperature, the sensitivity increased almost linearly with increasing the concentration of NH3 gas from 1-100 mu L/L.