Abstract:In order to improve the wear and corrosion resistance of Ti-6Al-4V, a novel beta-Ta2O5 nanoceramic coating was synthesised using reactive sputter deposition enabled by double glow discharge plasma technique. The surface topography, chemical composition, and microstructure of the newly developed coating were characterised by a variety of surface analytical techniques. The coating microstructure was found to exhibit a compact striated pattern extending in a direction perpendicular to coating surface, which is composed of equiaxed beta-Ta2O5 grains with an average grain size of similar to 20 nm, well adhered to the Ti-6A1-4V substrate. The hardness and the Young's modulus of the as-deposited coating were obtained by nanoindentation, and the adhesion strength between the coating and substrate was determined by a scratch tester. The dry sliding wear behaviours of the coating were investigated at room temperature against Si3N4 ceramic balls at room temperature under applied loads ranging from 2.3 N to 5.3 N using a ball-on-disc tribometer. The specific wear rates of the coating exhibited only a slight increase with applied normal load, and were shown to be two orders of magnitude lower than that for Ti-6Al-4V under the same loading condition. Furthermore, the electrochemical behaviour of the coating immersed in 3.5 wt.% NaCl solution was systematically examined by using a range of complementary electrochemical techniques including potentiodynamic polarisation, electrochemical impedance spectroscopy (EIS), MottSchottky analysis as well as potential of zero charge (PZC). The results showed that the corrosion resistance of the beta-Ta2O5 nanoceramic coating was better than that of Ti-6Al-4V alloy in 3.5 wt.% NaCl solution. Hence, by possessing higher mechanical properties and good wear and corrosion resistance, the beta-Ta2O5 nanoceramic coating is considered to be a promising candidate for protection of engineering components operating under harsh conditions. (C) 2016 Elsevier B.V. All rights reserved.

The Effect of TiN Coating on Erosion–corrosion Resistance of Α-Ti Alloy in Saline Slurry

Slurry erosion characteristics of TiN coatings on α-Ti and plasma-nitrided Ti alloy substrates

Slurry Erosion Behavior of TiN Coatings on Plasma-Nitrided Ti Alloy Substrates

Effect of Nitrogen Protective Atmosphere on Microstructure and High Temperature Erosion Property of TiAl3 and Cr3C2 Composite Coatings

High Temperature Erosion Properties of Arc-Sprayed Coatings Using Various Cored Wires Containing Ti–Al Intermetallics

Wear and Failure Analysis of Ti-6Al-4V Titanium Alloy with a Protective Coating during High-Speed Erosion

The Role of Ti in Cavitation Erosion and Corrosion Behaviours of NAB Alloy in 3.5 % NaCl Solution

Influence of the substrate hardness on the cavitation erosion resistance of TiN coating

Solid particle erosion behavior and failure mechanism of TiZrN coatings for Ti-6Al-4V alloy

Surface tribological and electrochemical properties of TiAlSiN coating in seawater

A Comparative Study of Erosion Wear Performance of Thermally Sprayed Ni-Based Composite Coatings

Corrosion and Wear Behaviours of a Reactive-Sputter-deposited Ta2O5 Nanoceramic Coating

Effects of Substrate Composition and Treatment Times on the Erosive Wear of Titanium Aluminide Coating: Prepared By Pack Cementation

Erosion Performance of TiN/Ti Coatings under Different Nitrogen Flow Rates

A comparative analysis of different surface tribological and electrochemical properties of TiAlN, TiAlSiN, and CrAlN thin film coatings in seawater

Structure Optimization and Failure Mechanism of Metal Nitride Coatings for Enhancing the Sand Erosion Resistance of Aluminum Alloys

Designed Ti/TiN sub-layers suppressing the crack and erosion of TiAlN coatings

Slurry erosion behaviour of AlCoCrFeNi high entropy alloy coating prepared by atmospheric plasma spraying

Microstructure and Properties of TiAlN Coating Prepared by Magnetron Sputtering on Titanium Alloy

Effect of Al Content on High Temperature Erosion Properties of Arc-Sprayed FeMnCrAl/Cr3C2 Coatings

Tribological Properties and Preparation of (Ti,Al)N Coatings on High Speed Steel Substrate