Abstract:Stable cationic waterborne polyurethanes (CWPUs) with a high solid content (HSC) were synthesized via the combination of cationic ionic and nonionic segments (polyoxyethylene alkyl amine, PAE). The process was based on an iterative strategy to design the cationic groups in soft segments and the chain terminal of polyurethanes (terminal ions) together with the determination of the optimal bimodal particle size distribution (PSD). The effects of the polymerization degree of poly(ethylene glycol) groups (PEG-g) in PAE and its interaction with the hydrophilic groups N-methyl diethanolamine (MDEA) in polyurethane were studied. It was found that the terminal ions resulted in a much finer dispersion, better dispersion stability, smaller particle size and lower viscosity. Moreover, the highest solid content (52.18%) of CWPU was obtained by the incorporation of PAE and a low terminal ions content of 2.5%, which had a bimodal particle size distribution. The increasing length of PEG-g was also found to enhance the thermal stability and render a better mechanical stability for the polyurethane films as the increasing PEG-g length may weaken the hydrogen bonding and reduce the extent of phase separation. The experimental results were further compared with molecular dynamic simulation results, which verified that the specific molecular structure of this WPU ensured its excellent properties. The static structure and dynamic properties obtained strongly supported the experimental observations reported on the morphology and thermal and mechanical properties of these polyurethanes.

Seeded-Emulsion Polymerization of Styrene with Waterborne Polyurethane Stabilizer Via Co-60 Gamma Ray

Preparation of Monodisperse Polystyrene Particles by Radiation-Induced Dispersion Polymerization Using Waterborne Polyurethane As a Stabilizer

Gamma-ray initiated miniemulsion polymerization of styrene stabilized by waterborne polyurethane

Simultaneous Interpenetrating Polymer Networks of Polyurethane from Pentaerythritol–Modified Castor Oil and Polystyrene: Structure–Property Relationships

The 60Co-Γ Ray-Initiated Seeded-Emulsion Polymerization of Methyl Methacrylate in the Presence of Waterborne Polyurethane Seeds

Synthesis of High-Toughness Waterborne Polyurethane Utilizing Self-Emulsifying CO2-based Polyols

Radiation‐induced Dispersion Polymerization of Methyl Methacrylate Using Waterborne Polyurethane As Stabilizer

Miniemulsion Polymerization of Styrene Costabilized with Polyurethane Via 60co Γ-Ray Radiation Initiation

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Preparation of polystyrene latex particles by γ-rays-induced emulsifier-free emulsion polymerization

PARTICLE FEATURES AND FORMATION MECHANISM OF POLYSTYRENE-POLY(METHYL METHACRYLATE) COMPOSITE PARTICLES PREPARED BY SUSPENSION-EMULSION COMBINED POLYMERIZATION

Synthesis and characterization of waterborne polyurethane emulsions based on poly(butylene itaconate) ester

Styrene mini-emulsion polymerization co-stabilized by predissolved fluoropolymer

Synthesis of Fluorinated Polyurethane/Polyacrylate Hybrid Emulsion Initiated By60co Γ-Ray and Properties of the Latex Film

Preparation of Polystyrene Particles with Narrow Particle Size Distribution by Γ-Ray Initiated Miniemulsion Polymerization Stabilized by Polymeric Surfactant

Synthesis and modification of waterborne polyurethane derived from hybrid CO2-based polyols

Preparation and Properties of High Solid Content and Low Viscosity Waterborne Polyurethane—Acrylate Emulsion with a Reactive Emulsifier

Controlled Radical Emulsion Polymerization of Polystyrene

Preparation and Characterization of Core–shell Polystyrene–polydimethylsiloxane Particles by Seeded Polymerization

Synthesis of stable cationic waterborne polyurethane with a high solid content: insight from simulation to experiment

Preparation and properties study of waterborne polyurethane synthesized by mixing polyester diols and isocyanates