Abstract:In this study, the oxygen evolution kinetics and oxide layer properties of Pb–0.8%Ag rolled-alloy anodes were investigated during 15d of galvanostatic electrolysis in an acidic zinc sulfate electrolyte solution containing 600mg·L−1 Cl− ions. Cyclic voltammetry, quasistationary polarization, and electrochemical impedance spectroscopy were used to investigate the anode process. The microscopic morphology and phase composition of the anodic oxide layers were observed by scanning electron microscopy and X-ray diffraction, respectively. The observable variations in the electrocatalytic activity and reaction kinetics of the anodes during electrolysis indicate the formation and stabilization of the anodic oxide layer. With prolonged electrolysis, the oxygen evolution overpotential in the anodes mainly exhibited a decreasing trend, which is contrary to the trend of the electrode surface exchange current density. This depolarization may have been caused by the increasing roughness of the anodic surface and the catalytic effects of α-PbO2 and β-PbO2. As electrolysis continued, the cathodic peak (α-PbO2→PbSO4) mainly showed an increasing trend and gradually moved toward the negative direction. After 15days of electrolysis, the oxide layers exhibited a severely corrosive microstructure with plenty of cavities and etch pits. The uniform, well-defined crystal grains and regularity were not appeared. The phase composition of the anodic oxide layer was formed after 6d of electrolysis. α-PbO2 proved to be the main peak and showed preferential growth orientations along the (111) planes of the anodic oxide layer.

Anodic Reaction Kinetics of Electrowinning Zinc in System of Zn(Ii)-Nh3-Nh4cl-H2o

EIS analysis on the anodic process of zinc in an alkaline solution

RESEARCH ON KINETICS OF TREATMENT OF ELECTROLYTIC ZINC WASTEWATER BY ELECTRODEPOSITION

Diffusion Coefficient of Ho3+at Liquid Zinc Electrode and Co-reduction Behaviors of Ho3+ and Zn2+ on W Electrode in the LiCl-KCl Eutectic

Electrochemical denitrification and kinetics study using Ti/IrO2-TiO2-RuO2 as the anode and Cu/Zn as the cathode

Anodic behavior of Fe in acidic AlCl3-EMIC ionic liquid

Revealing the Reaction Mechanism of Lead Anodes in the Manganese Electrowinning Process

On the Deposition and Dissolution of Zinc in Alkaline Solutions

Anodic Behavior of Pb-Ag-Ca-Sr Alloy in Zinc Electrowinning

A Chronocoulometric Method to Measure the Corrosion Rate on Zinc Metal Electrodes

OXIDATION KINETICS OF ANILINE BY ZINC DICHROMATE

Preparation and electrochemical properties of a novel porous Ti/Sn–Sb-RuO x /β-PbO 2 /MnO 2 anode for zinc electrowinning

Electrochemical Behavior of Rolled Pb–0.8%Ag Anodes in an Acidic Zinc Sulfate Electrolyte Solution Containing Cl− Ions

Properties of Al/conductive coating/α-PbO2-CeO2-TiO2/β-PbO2-WC-ZrO2 composite anode for zinc electrowinning

Nickel electrowinning using a Pt catalysed hydrogen-diffusion anode. Part I: Effect of chloride and sulfate ions and a magnetic field

Electrochemical study of active dissolution for aluminum in neutral NaCl solution

Mechanisms Investigation of Cathodic-Anodic Coupling Reaction of Zr-H2O at 360 °C by Long-Term In-Situ Electrochemical Polarization Analyses

Influence of Cathodic Overpotential and Zincate Concentration on Zinc Deposition in Alkaline Solution

Electrochemical dissolution of nickel-42 in acid electrolytes

Process and Anodic Reaction Mechanism of Cadmium Electrically Enhanced Cementation on Zinc Plate under an Ultrasonic Field in Ammoniacal System

Influence of Concentration of Zinc Ions on Electrocrystallization Process of Zinc