Growth And Characterization Of Nd-Doped Ca0.28ba0.72nb2o6 Crystal
Wenlan Gao,Huaijin Zhang,Dongxu Liu,Min Xu,Jiyang Wang,Yonggui Yu,Minhua Jiang,Shangqian Sun,Hairui Xia,Robert I. Boughton
DOI: https://doi.org/10.1063/1.3054583
IF: 2.877
2009-01-01
Journal of Applied Physics
Abstract:We report the growth of a Nd-doped calcium barium niobate (Nd:CBN-28) single crystal using the Czochralski method. The point group and space group of Nd:CBN-28 are determined to be tetragonal 4mm and P4bm, respectively, and the effective segregation coefficients of Nd, Ca, Ba, and Nb are 0.988, 1.029, 0.992, and 0.985, respectively. The density of the material is 5.321 g cm(-3) at 19.6 degrees C, in good agreement with the theoretical value. Thermal expansion measurements reveal that during the heating cycle, the c-axis of Nd:CBN-28 undergoes both thermal contraction and thermal expansion, while at the same time there is only expansion along the a-axis. Specific heat measurements reveal that an anomaly appears at about 220 degrees C due to a phase transition. The thermal diffusivity increases slowly with increasing temperature. The thermal conductivity of the crystal has been calculated from these results, and the phonon mean free paths l(a) and l(c) along the a- and c-axes of Nd:CBN-28 crystal are estimated. The transmission spectrum of Nd:CBN-28 crystal along the [001] direction has been measured.