Growth and Magneto-Optical Properties of NaTb(WO4)2

Jingjing Liu,Feiyun Guo,Bin Zhao,Naifeng Zhuang,Yanping Chen,Zhaoping Gao,Jianzhong Chen

DOI: https://doi.org/10.1016/j.jcrysgro.2007.12.065

IF: 1.8

2008-01-01

Journal of Crystal Growth

Abstract:Sodium terbium tungstate (NaTb(WO4)2) single crystal with dimension ∅ 25mm×30mm and a good optical quality was grown by Czochralski method. The transmission spectrum was measured in the visible and near-infrared region at room temperature. The specific Faraday rotation of single crystal was measured at room temperature in 532, 633, and 1064nm wavelength. The Verdet constant and magneto-optical figure of merit was investigated. Comparing to the magneto-optical figure of merit and Verdet constant for TGG, the NaTb(WO4)2 have larger magneto-optical figure of merit and larger Verdet constant. It indicates that NaTb(WO4)2 crystal can be a promising magneto-optical material in visible region.